PC LUPOY® GN2301F KA02 LG GUANGZHOU

Unit Price:
$3725 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	300°C/1.2 kg	ASTM D1238	5.0	g/10 min
Modeling Shrinkage - Flow	23°C, 3.20 mm, Injection	ASTM D955	0.10 到 0.30	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus	23°C, 3.20 mm, Injection	ASTM D790	6860	Mpa
Flexural Strength	23°C, 3.20 mm, Injection	ASTM D790	177	Mpa
Tensile Strength	Yield, 23°C, 3.20 mm, Injection	ASTM D638	118	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
RTI		UL 746	105	°C
RTI Imp		UL 746	90.0	°C
RTI Elec		UL 746	120	°C
Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm, Injection	ASTM D648	142	°C

Injection	Test Result	Unit
Drying Time	3.0 到 5.0	hr
Rear Temperature	270 到 300	°C
Middle Temperature	280 到 310	°C
Front Temperature	290 到 330	°C
Nozzle Temperature	290 到 330	°C
Back Pressure	0.981 到 3.92	Mpa
Screw Speed	40 到 70	rpm
Drying Temperature	100 到 200	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	300 到 340	°C
Mold Temperature	90 到 120	°C

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R-Scale, 23°C, Injection	ASTM D785	120

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	1.5 mm	UL 94	V-0
Flame Rating	Flame Rating	3.0 mm	UL 94	V-0 5VA

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.