Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt flow index | ℃/Kg | ASTMD1238 | 1.0 | g/10min |
| Melt flow index | 厚度 | | 25.4 | microns |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile elongation at break (MD) | 25.4um | ASTM D-882 | 520 | % |
| Tensile elongation at break (TD) | 25.4um | ASTM D-882 | 660 | % |
| Elmendorf Tear Strength (TD) | 25.4um | ASTM D-1922 | 410 | g |
| Elmendorf Tear Strength (MD) | 25.4um | ASTM D-1922 | 71 | g |
| Tensile fracture strength (TD) | 25.4um | ASTM D-882 | 33.1 | Mpa |
| Tensile strength at break (MD) | 25.4um | ASTM D-882 | 38.3 | Mpa |
| tensile strength | | ASTMD882 | 15.23 | Mpa |
| tensile strength | | ASTMD882 | 16.72 | Mpa |
| tensile strength | | ASTMD882 | 38.34 | Mpa |
| tensile strength | | ASTMD882 | 33.13 | Mpa |
| elongation | Break | ASTMD882 | 522 | % |
| elongation | Break | ASTMD882 | 656 | % |
| Tensile yield strength (TD) | 25.4um | ASTM D-882 | 16.7 | Mpa |
| Tensile yield strength (MD) | 25.4um | ASTM D-882 | 15.2 | Mpa |
| Elmendorf tear strength | | ASTMD192 | 413 | g |
| Elmendorf tear strength | | ASTMD192 | 71 | g |
| Secant modulus | | ASTMD882 | 377.3 | Mpa |
| Secant modulus | | ASTMD882 | 348.5 | Mpa |
| Falling hammer impact | 25.4um | ASTM D-1709A | 110 | g |
| Falling hammer impact | | ASTMD1709 | 112 | g |
| impact force | | | 93 | ft-lbf/in3 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ASTM1525 | 120 | °C |
| Vicat softening temperature | Melting Temperature | 陶氏化学方法(DSC | 126 | °C |
| Melting temperature | | Internal Method | 126 | °C |
| vicat softening point | | ASTM D-1525 | 120 | °C |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Temperature | | | 204-246 | °C |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Film Piercing Resistance Movement | 25.4um | Internal Method | 7.69 | J/cm³ |
| Film Resilience (MD) | 25.4um | ASTM D-882 | 97.5 | J/cm³ |
| Film Resilience (TD) | 25.4um | ASTM D-882 | 115 | J/cm4 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | 25.4um | ASTM D-1003 | 7 | % |
| gloss | 45°，25.4um | ASTM D-2457 | 58 | |
| gloss | | ASTM2457 | 58 | |
| Haze μ m | | ASTMD1003 | 7.0 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt flow rate | 190℃/2.16kg | ASTM D-1238 | 1 | g/10min |
| density | | ASTM D-792 | 0.935 | g/m3 |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Elmendorf tear strength | | ASTMD1922 | 2.80 | g/micron |
| Elmendorf tear strength | | ASTMD1922 | 16.3 | g/micron |
| impact force | | ASTMD882 | 1178 | ft-lbf/in3 |
| impact force | | ASTMD882 | 1389 | ft-lbf/in3 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.