Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Flow : 0.750 to 2.30 mm | 内部方法 | 0.80 到 1.1 | % |
| Modeling Shrinkage | Flow : 2.30 to 4.60 mm | 内部方法 | 1.0 到 1.4 | % |
| Modeling Shrinkage | Across Flow : 0.750 to 2.30 mm | 内部方法 | 0.90 到 1.3 | % |
| Modeling Shrinkage | Across Flow : 2.30 to 4.60 mm | 内部方法 | 1.2 到 1.6 | % |
| Moisture Absorption | 24 hr | ASTM D570 | 0.080 | % |
| Specific Volume | | ASTM D792 | 0.750 | cm³/g |
| Outdoor Suitability | | UL 746C | f1 | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Elongation | Break | ASTM D638 | 110 | % |
| Flexural Modulus | 50.0 mm Span | ASTM D790 | 2060 | Mpa |
| Tensile Strength | Yield | ASTM D638 | 48.0 | Mpa |
| Tensile Strength | Break | ASTM D638 | 48.0 | Mpa |
| Flexural Strength | Yield, 50.0 mm Span | ASTM D790 | 82.0 | Mpa |
| Flexural Strength | Break, 50.0 mm Span | ASTM D790 | 82.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Coefficient of Linear Thermal Expansion (Flow) | -40 to 40°C | ASTM E831 | 9.2E-5 | cm/cm/°C |
| Coefficient of Linear Thermal Expansion (Flow) | 60 to 138°C | ASTM E831 | 1.2E-4 | cm/cm/°C |
| RTI | | UL 746 | 140 | °C |
| RTI Imp | | UL 746 | 120 | °C |
| RTI Elec | | UL 746 | 120 | °C |
| Deflection Temperature Under Load? | 0.45 MPa, Unannealed, 6.40 mm | ASTM D648 | 137 | °C |
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 6.40 mm | ASTM D648 | 98.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Constant | 100 Hz | ASTM D150 | 3.20 | |
| Dielectric Constant | 1 MHz | ASTM D150 | 3.20 | |
| Volume Resistivity | | ASTM D257 | > 1.2E+16 | ohms·cm |
| Dissipation Factor? | 100 Hz | ASTM D150 | 3.0E-3 | |
| Dissipation Factor? | 1 MHz | ASTM D150 | 0.030 | |
| Dielectric Strength | 1.60 mm, in Oil | ASTM D149 | 25 | KV/mm |
| Dielectric Strength | 3.20 mm, in Air | ASTM D149 | 19 | KV/mm |
| Dielectric Strength | 3.20 mm, in Oil | ASTM D149 | 19 | KV/mm |
| Comparative Tracking Index | | UL 746 | PLC 2 | |
| Hot-wire Ignition | | UL 746 | PLC 2 | |
| High Amp Arc Ignition | | UL 746 | PLC 3 | |
| High Voltage Arc Tracking Rate | | UL 746 | PLC 3 | |
| Arc Resistance | | ASTM D495 | PLC 6 | |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Time | | | 3.0 到 4.0 | hr |
| Suggested Shot Size | | | 40 到 80 | % |
| Rear Temperature | | | 240 到 255 | °C |
| Middle Temperature | | | 245 到 260 | °C |
| Front Temperature | | | 250 到 265 | °C |
| Nozzle Temperature | | | 245 到 260 | °C |
| Back Pressure | | | 0.300 到 0.700 | Mpa |
| Screw Speed | | | 50 到 100 | rpm |
| Vent Depth | | | 0.025 到 0.038 | mm |
| Drying Temperature | | | 120 | °C |
| Suggested Max Moisture | | | 0.020 | % |
| Processing (Melt) Temp | | | 250 到 265 | °C |
| Mold Temperature | | | 50 到 75 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Unnotched Izod Impact Strength | 23°C | ASTM D4812 | 3200 | J/m |
| Gardner Impact | 23°C | ASTM D3029 | 43.0 43.0 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Scale | ASTM D785 | 117 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Index | | ASTM D2863 | 30 | % |
| Flame Rating | 0.46 mm | UL 94 | HB | |
| Flame Rating | 0.64 mm | UL 94 | V-0 | |
| Flame Rating | 3.0 mm | UL 94 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.