Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 2.5 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile yield strength (MD) | 25.4um | ASTM D-882 | 17.6 | Mpa |
| Tensile yield strength (MD) | 25.4um | ASTM D-882 | 16.9 | Mpa |
| Tensile fracture strength (TD) | 25.4um | ASTM D-882 | 39.9 | Mpa |
| Tensile strength at break (MD) | 25.4um | ASTM D-882 | 59.2 | Mpa |
| Tensile elongation at break (MD) | 25.4um | ASTM D-882 | 620 | % |
| Tensile elongation at break (TD) | 25.4um | ASTM D-882 | 750 | % |
| Falling hammer impact | 25.4um | ASTM D-1709A | 57 | g |
| Elmendorf Tear Strength (MD) | 25.4um | ASTM D-1922 | 83 | g |
| Elmendorf Tear Strength (TD) | 25.4um | ASTM D-1922 | 290 | g |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| vicat softening point | | ASTM D-1525 | 119 | °C |
| Melting temperature | | Internal Method | 125 | °C |
| Vicat softening temperature | | ASTMD1525 | 119 | °C |
| Melting temperature (DSC) | | 内部方法 | 125 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| elongation | MD:Break,25μm | ASTMD882 | 620 | % |
| elongation | TD:Break,25μm | ASTMD882 | 750 | % |
| Falling hammer impact | 25µm | ASTMD1709A | 57 | g |
| Elmondov tear strength | MD:25µm | ASTMD1922 | 83 | g |
| Elmondov tear strength | TD:25µm | ASTMD1922 | 290 | g |
| Film thickness - tested | | | 25 | µm |
| Membrane puncture resistance | 25µm | 内部方法 | 10.3 | J/cm³ |
| Membrane strength | MD:25µm | ASTMD882 | 324 | J/cm³ |
| Membrane strength | TD:25µm | ASTMD882 | 308 | J/cm³ |
| Tensile strength | MD:Yield,25μm | ASTMD882 | 16.9 | Mpa |
| Tensile strength | TD:Yield,25μm | ASTMD882 | 17.6 | Mpa |
| Tensile strength | MD:Break,25μm | ASTMD882 | 59.2 | Mpa |
| Tensile strength | TD:Break,25μm | ASTMD882 | 39.9 | Mpa |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Temperature | | | 274 | °C |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Film Piercing Resistance Movement | 25.4um | Internal Method | 10.3 | J/cm³ |
| Film Resilience (MD) | 25.4um | ASTM D-882 | 324 | J/cm³ |
| Film Resilience (TD) | 25.4um | ASTM D-882 | 308 | J/cm4 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| gloss | 45°，25.4um | ASTM D-2457 | 90 | |
| Haze | 25.4um | ASTM D-1003 | 2.6 | % |
| gloss | 45°,25.4µm | ASTMD2457 | 90 | |
| Haze | 25.4µm | ASTMD1003 | 2.6 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D-792 | 0.935 | g/m3 |
| Melt flow rate | | ASTM D-1238 | 2.5 | g/10min |
| film thickness | | | 25.4 | um |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.