Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Moisture Absorption | -,23C/59RH | % | ISO 62 | |
-,Sat/23C | % | ISO 62 | 0.2 | |
Modeling Shrinkage | -,Across Flow | % | ISO 294-4 | 1.6 |
-,Flow | % | ISO 294-4 | 1.8 | |
Density / Specific Gravity | g/cm | ISO 1183 | 1.45 | |
ISO1183 | 1.45 | g/cm³ | ||
Modeling Shrinkage | TD | ISO294-4 | 1.6 | % |
MD | ISO294-4 | 1.8 | % | |
Moisture Absorption | Saturation,23°C,2.00mm | ISO62 | 0.35 | % |
Equilibrium,23°C,2.00mm,50%RH | ISO62 | 0.20 | % | |
MediumDensity | 1.25 | g/cm³ | ||
Ejection Temperature | 170 | °C | ||
SpecificHeatCapacityofMelt | 1850 | J/kg/°C | ||
ThermalConductivityofMelt | 0.25 | W/m/K |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Stress | Break | ISO527-2 | 47.0 | Mpa |
Tensile Strain | Break | ISO527-2 | 10 | % |
Tensile Creep Modulus | 1hr | ISO899-1 | 3500 | Mpa |
Tensile Creep Modulus | 1000hr | ISO899-1 | 2400 | Mpa |
Flexural Stress | ISO178 | 90.0 | Mpa | |
Tensile Modulus | ISO527-2 | 3500 | Mpa | |
Tensile Creep Modulus | -,1h | MPa | ISO 899-1 | 3500 |
-,1000h | MPa | ISO 899-1 | 2400 | |
Charpy Notched Impact Strength | -,-30℃, Type 1, Edgewise | KJ/m | ISO 179 | |
-,23℃, Type 1, Edgewise | KJ/m | ISO 179 | ||
Charpy Notched Impact Strength | -,-30℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | |
-,23℃, Type 1, Edgewise, Notch A | KJ/m | ISO 179 | ||
Tensile Stress (Break) | MPa | ISO 527-1, -2 | 47 | |
Tensile Strain (Break) | 23℃, 5 mm/min | % | ISO 527-1, -2 | |
Tensile Modulus | 23 ℃, 1.0 mm/min | MPa | ISO 527-1, -2 | 3500 |
Flexural Strength | 23℃ | MPa | ISO 178 | |
Unnotched Izod Impact Strength | 23 ℃, Type 1 | KJ/m | ISO 180 | 37 |
Notched Impact Strength | 23℃, Type 1, Notch A | KJ/m | ISO 180 |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Coefficient of Linear Thermal Expansion | 平行Flow ,23 to 55℃(73 to 130°F) | cm/cm/℃ | ISO 11359-1, -2 | |
垂直Flow ,23 to 55℃(73 to 130°F) | cm/cm/℃ | ISO 11359-1, -2 | ||
Deflection Temperature Under Load? | -,0.45 Mpa,Unannealed | ℃ | ISO 75B-1, -2 | 185 |
Flame Rating | -,3.00 mm | UL 94 | HB | |
Melting temperature | ℃ | ISO 3146 | 225 | |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 165 | °C |
1.8MPa,Unannealed | ISO75-2/A | 65.0 | °C | |
Vicat Softening Temperature | ISO306/B50 | 195 | °C | |
Melting Temperature | ISO11357-3 | 225 | °C | |
Linear thermal expansion coefficient | MD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
TD | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
Deflection Temperature Under Load? | -,1.80 Mpa,Unannealed | ℃ | ISO 75A-1, -2 | |
Flame Rating | -,1.50 mm | UL 94 | HB |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Volume Resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
Dielectric Strength | IEC60243-1 | 25 | KV/mm | |
Relative Permittivity | 100Hz | IEC60250 | 4.00 | |
1MHz | IEC60250 | 3.70 | ||
Dissipation Factor? | 100Hz | IEC60250 | 9E-03 | |
1MHz | IEC60250 | 0.016 | ||
Comparative Tracking Index | IEC60112 | 250 | V |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 3.5 | kJ/m² |
23°C | ISO179/1eA | 3.5 | kJ/m² | |
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 50 | kJ/m² |
23°C | ISO179/1eU | 40 | kJ/m² | |
Notched Izod Impact Strength | -30°C | ISO180/1A | 4.0 | kJ/m² |
23°C | ISO180/1A | 3.5 | kJ/m² | |
Notched Izod impact strength | -30°C | ISO180/1U | 34 | kJ/m² |
23°C | ISO180/1U | 37 | kJ/m² |
Other | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Oxygen Index | % | ISO 4589-1, -2 | 22 |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Burning Rate | 1.00mm | ISO3795 | 24 | mm/min |
UL flame retardant rating | 1.5mm | UL94 | HB | |
3.0mm | UL94 | HB | ||
1.5mm | IEC60695-11-10,-20 | HB | ||
3.0mm | IEC60695-11-10,-20 | HB | ||
Oxygen Index | ISO4589-2 | 22 | % | |
FMVSS Flammability | FMVSS302 | SE/B | ||
Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.