Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTM D792/ISO 1183 | 1.19 | |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 250°C/2.16kg | ISO1133 | 20 | g/10min |
| Modeling Shrinkage | MD | 内部方法 | 0.40to0.60 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Yield | ISO527-2/50 | 62.0 | Mpa |
| Tensile Strain | Break | ISO527-2/50 | >20 | % |
| Tensile Modulus | | ISO527-2/1 | 2500 | Mpa |
| Rockwell Hardness | | ASTM D785 | 113 | |
| Flexural Modulus | | ASTM D790/ISO 178 | 2650 | kg/cm²(MPa)[Lb/in²] |
| Flexural Strength | | ASTM D790/ISO 178 | 93.2 | kg/cm²(MPa)[Lb/in²] |
| Flexural Modulus | | ISO178 | 2600 | Mpa |
| Flexural Stress | | ISO178 | 93.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ISO306/B50 | 99.0 | °C |
| Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 103 | ℃（℉） |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 91.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | NoBreak | |
| Notched Izod Impact Strength | 23°C | ISO180 | 13 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.2mm | UL94 | V-0 | |
| UL flame retardant rating | 1.5mm | UL94 | 5VB | |
| UL flame retardant rating | 2.5mm | UL94 | 5VA | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.