PBT LNP™ LUBRICOMP™ WFL-4034 SABIC INNOVATIVE US
84
- Unit Price:
- $8051 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Aging resistance Filler: Glass fiber reinf 20% filler by weight
- Application Areas:Electrical field Automotive components
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：24hr | ASTMD955 | 0.30to0.50 | % |
| Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.054 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.072 | % | |
| Modeling Shrinkage | TD：24hr | ASTMD955 | 1.0to3.0 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | ISO178 | 7070 | Mpa | |
| Flexural Strength | Break,50.0mmSpan | ASTMD790 | 173 | Mpa |
| Coefficient of Friction | Dynamic | ASTMD3702Modified | 0.24 | |
| Specific Wear Rate | Washer | ASTMD3702Modified | 44.5 | 10^-10in^5-min/ft-lb-hr |
| Flexural Modulus | 50.0mmSpan | ASTMD790 | 7480 | Mpa |
| Specific Wear Rate | Ring | ASTMD3702Modified | -0.0200to-0.0100 | 10^-10in^5-min/ft-lb-hr |
| Tensile Strain | Yield | ISO527-2/5 | 2.6 | % |
| Tensile Stress | Yield | ISO527-2/5 | 114 | Mpa |
| Tensile Modulus | ISO527-2/1 | 7890 | Mpa | |
| Tensile Strength | Break | ASTMD638 | 118 | Mpa |
| Yield | ASTMD638 | 118 | Mpa | |
| Coefficient of Friction | Static | ASTMD3702Modified | 0.22 | |
| Tensile Modulus | ASTMD638 | 8270 | Mpa | |
| Tensile Strain | Break | ISO527-2/5 | 2.6 | % |
| Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 173 | Mpa |
| Tensile Stress | Break | ISO527-2/5 | 114 | Mpa |
| Tensile Elongation | Yield | ASTMD638 | 2.6 | % |
| Tensile Elongation | Break | ASTMD638 | 2.6 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 222 | °C |
| Linear thermal expansion coefficient | TD：-30to30°C | ASTMD696 | 8.9E-05 | cm/cm/°C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 210 | °C |
| Linear thermal expansion coefficient | MD：-30to30°C | ASTMD696 | 3.6E-05 | cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 222 | °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 208 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Multi-Axial Instrumented Impact Energy | ISO6603-2 | 2.90 | J | |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 41 | kJ/m² |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 7.50 | J |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 7.8 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.