PPA AMODEL® AS-4133 HS BK324 SOLVAY USA
180
- Unit Price:
- $7485 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 41MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Flame retardant Thermal stability Filler: Glass fiber reinf 33% filler by weight
- Application Areas:Automotive components Sports equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flow,23℃,50%RH | % | 0.21到1.2 | ||
| 23℃ | % | 0.14到1.0 | ||
| g/cm³ | 1.29到1.78 | |||
| 23℃,24hr | % | 0.30到0.51 | ||
| % | 0.12到0.30 | |||
| Flow:23℃ | mm/mm | 119.4E-3到0.254 | ||
| Flow:23℃ | mm/mm | 48.3E-3到129.5E-3 | ||
| -- | 1.33到1.73 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compressive Strength | 23℃ | MPa | 142.76到196.55 | |
| Shearing Strength | 23℃ | MPa | 88.28到107.59 | |
| Poisson Ratio | 23℃ | 0.41 | ||
| Tensile Modulus | 摩擦系数 | 0.15到0.52 | ||
| 23℃ | MPa | 8827.59到14482.76 | ||
| MPa | 5137.93到18620.69 | |||
| MPa | 126.21到364.14 | |||
| MPa | 5337.93到17586.21 | |||
| MPa | 5200.0到18344.83 | |||
| MPa | 88.28到260.0 | |||
| MPa | 137.93到392.41 | |||
| Break,23℃ | MPa | 108.28到262.76 | ||
| MPa | 162.76到199.31 | |||
| % | 1.5到3.1 | |||
| % | 1.0到2.5 | |||
| MPa | 131.72到400.0 | |||
| Yield,23℃ | MPa | 68.97到250.34 | ||
| MPa | 102.76到362.76 | |||
| % | 1.4到2.5 | |||
| % | 1.5到2.6 | |||
| MPa | 12.62到270.34 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | °C | 258到313 | ||
| RTIElec | °C | 140到150 | ||
| Evolution Calendar intelligent importer | °C | 118到150 | ||
| 0.45MPa, Unannealed | °C | 273到312 | ||
| °C | 275到308 | |||
| 1.8MPa, Unannealed | °C | 249到304 | ||
| °C | 247到292 | |||
| Continuous Use Temperature | °C | 140到186 | ||
| 8.0Mpa, Unannealed | °C | 165到230 | ||
| Flow | mm/mm/°C | 63.5E-5到177.8E-5 | ||
| mm/mm/°C | 68.6E-5到127.0E-5 | |||
| Flow | mm/mm/°C | 185.4E-5到25.4E-5 | ||
| mm/mm/°C | 38.1E-5到50.8E-5 | |||
| mm/mm/°C | 195.6E-5到25.4E-5 | |||
| 0.45MPa Annealed | °C | 296到320 | ||
| 1.8MPa, Unannealed | °C | 283到300 | ||
| RTI | °C | 119到150 | ||
| -- | °C | 299到315 | ||
| °C | 310到312 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| -- | ohms | 1.0E+5到2.5E+16 | ||
| ohms | 1.0E+2到2.5E+15 | |||
| 23℃ | V/mil | 450到590 | ||
| 3.66 | ||||
| ohms·cm | 1.0E+3到2.5E+15 | |||
| V/mil | 420到1100 | |||
| ohms·cm | 1.0E+15到2.6E+16 | |||
| 4.9E-3到0.015 | ||||
| 3.66到5.52 | ||||
| 4.0E-3到0.017 | ||||
| Comparative Tracking Index | CTI | V | 548到600 | |
| Comparative Tracking Index | V | 593到600 |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Unnotched Impact Strength | 23℃ | kJ/m² | 4.178到19.964 | |
| 23℃ | N.m | 138.05到788.50 | ||
| J/m | 0.008到0.042 | |||
| J | 0.78到2.04 | |||
| kJ/m² | 0.556到3.158 | |||
| kJ/m² | 4.365到15.786 | |||
| J/m | 0.066到0.351 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | 23℃ | 125 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Glow Wire Flammability Index | °C | 743到960 | ||
| Oxygen Index | % | 23到25 | ||
| Glow Wire Ignition Temperature | °C | 721到926 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.