PPA AMODEL® AS-1133HS NT SOLVAY USA

124

Unit Price:
$10788 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Filler: Glass fiber reinf 33% filler by weight
Application Areas:Lawn and garden equipment Power/Other Tools Valves/valve components Industrial components Industrial applications Thick wall accessories (c Machine/mechanical compon Metal substitution Connector Parts under the hood of a Vehicle electronics Application in the automo Fuel pipeline Oil/Gas Supplies currency Shell
Color:--
Grade:Injection grade

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD	ASTMD955	0.40	%
Shrinkage rate	Shrinkage rate	TD	ASTMD955	0.80	%
Water absorption rate	24hr	ASTMD570	0.21	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus		ASTMD638	13100	Mpa
Tensile modulus	Tensile modulus		ISO527-2	12200	Mpa
Tensile stress	Yield	ISO527-2	225	Mpa
Tensile strength	Break	ASTMD638	221	Mpa
elongation	Break	ASTMD638	2.5	%
Tensile strain	Break	ISO527-2	3.0	%
Bending modulus		ASTMD790	10300	Mpa
Bending modulus	Bending modulus		ISO178	10300	Mpa
Bending stress		ISO178	326	Mpa
bending strength	Yield	ASTMD790	317	Mpa
compressive strength		ASTMD695	276	Mpa
shear strength		ASTMD732	101	Mpa
Poisson's ratio		7.58	0.41

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Annealed,3.18mm	ASTMD648	297	°C
	Hot deformation temperature	1.8MPa,Annealed,3.18mm	ASTMD648	285	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Annealed	ISO75-2/Af	277	°C
Continuous use temperature	--2	ASTMD3045	164	°C
Continuous use temperature	Continuous use temperature	--3	ASTMD3045	185	°C
Peak melting temperature		ASTMD3418	310	°C
Melting temperature		ISO11357-3	310	°C
Linear coefficient of thermal expansion	MD：0to100°C	ASTME831	2.3E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD：160to249°C	ASTME831	1.4E-05	cm/cm/°C
		Linear coefficient of thermal expansion	TD：0to100°C	ASTME831	5.9E-05	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：160to249°C	ASTME831	1.3E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		ASTMD257	1E+16	ohms·cm
Dielectric strength	3.17mm	ASTMD149	21	KV/mm
Dielectric constant	60Hz	ASTMD150	4.40
Dielectric constant	Dielectric constant	1MHz	ASTMD150	4.20
Dissipation factor	60Hz	ASTMD150	5E-03
Dissipation factor	Dissipation factor	1MHz	ASTMD150	0.017
Arc resistance		ASTMD495	140	sec
Compared to the anti leakage trace index	CTI	UL746	550	V

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch		ISO179/1eU	82	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTMD785	125

optical performance	Test Condition	Test Method	Test Result	Unit
Transmittance 5	1070nm:1.60mm	ASTMD1003	>35	%
Transmittance 5	Transmittance 5	940nm:1.60mm	ASTMD1003	>30	%

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating 4	3.2mm	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.