Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTMD955 | 0.30 | % |
Modeling Shrinkage | TD | ASTMD955 | 0.60 | % |
Moisture Absorption | 24hr | ASTMD570 | 0.20 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield,23°C | ISO527-2 | 186 | Mpa |
Tensile Stress | Yield,100°C | ISO527-2 | 114 | Mpa |
Tensile Stress | Yield,150°C | ISO527-2 | 75.2 | Mpa |
Tensile Stress | Yield,175°C | ISO527-2 | 63.4 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 1.6 | % |
Tensile Strain | Break,24°C | ISO527-2 | 2.4 | % |
Tensile Strain | Break,150°C | ISO527-2 | 5.1 | % |
Tensile Strain | Break,175°C | ISO527-2 | 4.9 | % |
Flexural Stress | 23°C | ISO178 | 259 | Mpa |
Flexural Stress | 100°C | ISO178 | 161 | Mpa |
Flexural Stress | 150°C | ISO178 | 101 | Mpa |
Flexural Stress | 175°C | ISO178 | 87.6 | Mpa |
Tensile Modulus | | ASTMD638 | 16100 | Mpa |
Tensile Modulus | 23°C | ISO527-2 | 14500 | Mpa |
Tensile Modulus | 100°C | ISO527-2 | 9170 | Mpa |
Tensile Modulus | 150°C | ISO527-2 | 5930 | Mpa |
Tensile Modulus | 175°C | ISO527-2 | 5100 | Mpa |
Tensile Elongation | Break | ASTMD638 | 1.7 | % |
Flexural Modulus | | ASTMD790 | 13100 | Mpa |
Flexural Modulus | 23°C | ISO178 | 12600 | Mpa |
Flexural Modulus | 100°C | ISO178 | 8070 | Mpa |
Flexural Modulus | 150°C | ISO178 | 4960 | Mpa |
Flexural Modulus | 175°C | ISO178 | 4620 | Mpa |
Flexural Strength | | ASTMD790 | 224 | Mpa |
Compressive Strength | | ASTMD695 | 145 | Mpa |
Shearing Strength | | ASTMD732 | 80.0 | Mpa |
Tensile Strength | | ASTMD638 | 199 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Peak Melting Temperature | | ASTMD3418 | 310 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/Af | 282 | °C |
Deflection Temperature Under Load? | 1.8MPa,Annealed | ASTMD648 | 277 | °C |
Linear thermal expansion coefficient | MD:0to100°C | ASTME831 | 1.7E-05 | cm/cm/°C |
Linear thermal expansion coefficient | MD:100to200°C | ASTME831 | 7E-06 | cm/cm/°C |
Linear thermal expansion coefficient | TD:0to100°C | ASTME831 | 6.4E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:100to200°C | ASTME831 | 1.1E-04 | cm/cm/°C |
Melting temperature | | ISO11357-3 | 310 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | 3.17mm | ASTMD149 | 24 | KV/mm |
Surface Resistivity | | ASTMD257 | 1E+15 | ohms |
Dielectric Constant | 100Hz | ASTMD150 | 4.40 | |
Dielectric Constant | 1MHz | ASTMD150 | 4.10 | |
Volume Resistivity | | ASTMD257 | 1E+15 | ohms·cm |
Dissipation Factor? | 1MHz | ASTMD150 | 0.011 | |
Comparative Tracking Index | CTI | UL746 | PLC1 | |
High Amp Arc Ignition | 0.75mm | UL746 | PLC0 | |
High Amp Arc Ignition | 1.5mm | UL746 | PLC0 | |
High Amp Arc Ignition | 3.0mm | UL746 | PLC0 | |
Hot-wire Ignition | 0.75mm | UL746 | PLC0 | |
Hot-wire Ignition | 1.5mm | UL746 | PLC0 | |
Hot-wire Ignition | 3.0mm | UL746 | PLC0 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod impact strength | 23°C | ISO180/1U | 44 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 46 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.8mm | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.