Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD | ASTMD955 | 0.50 | % |
Modeling Shrinkage | TD | ASTMD955 | 1.0 | % |
Moisture Absorption | 24hr | ASTMD570 | 0.29 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break,23°C | ISO527-2 | 211 | Mpa |
Tensile Stress | Break,24°C | ISO527-2 | 125 | Mpa |
Tensile Stress | Break,150°C | ISO527-2 | 87.6 | Mpa |
Tensile Stress | Break,175°C | ISO527-2 | 79.3 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 2.6 | % |
Tensile Strain | Break,24°C | ISO527-2 | 4.3 | % |
Tensile Strain | Break,150°C | ISO527-2 | 6.6 | % |
Tensile Strain | Break,175°C | ISO527-2 | 6.6 | % |
Flexural Stress | 23°C | ISO178 | 296 | Mpa |
Flexural Stress | 100°C | ISO178 | 177 | Mpa |
Flexural Stress | 150°C | ISO178 | 111 | Mpa |
Flexural Stress | 175°C | ISO178 | 99.3 | Mpa |
Tensile Modulus | 23°C | ISO527-2 | 12600 | Mpa |
Tensile Modulus | 100°C | ISO527-2 | 6830 | Mpa |
Tensile Modulus | 150°C | ISO527-2 | 5310 | Mpa |
Tensile Modulus | 175°C | ISO527-2 | 4830 | Mpa |
Tensile Modulus | | ASTMD638 | 11700 | Mpa |
Tensile Elongation | Break | ASTMD638 | 2.5 | % |
Flexural Modulus | 23°C | ISO178 | 10400 | Mpa |
Flexural Modulus | 100°C | ISO178 | 7170 | Mpa |
Flexural Modulus | 150°C | ISO178 | 4620 | Mpa |
Flexural Modulus | 175°C | ISO178 | 4210 | Mpa |
Flexural Modulus | | ASTMD790 | 11000 | Mpa |
Flexural Strength | | ASTMD790 | 290 | Mpa |
Tensile Strength | | ASTMD638 | 200 | Mpa |
Compressive Strength | | ASTMD695 | 179 | Mpa |
Shearing Strength | | ASTMD732 | 89.6 | Mpa |
Poisson Ratio | | 7.58 | 0.41 | |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Continuous Use Temperature | | ASTMD3045 | 210 | °C |
Deflection Temperature Under Load? | 0.45MPa,Annealed,3.20mm | ASTMD648 | 320 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 294 | °C |
Deflection Temperature Under Load? | 1.8MPa,Annealed,3.20mm | ASTMD648 | 300 | °C |
Linear thermal expansion coefficient | MD:0to100°C | ASTME831 | 2E-05 | cm/cm/°C |
Linear thermal expansion coefficient | MD:100to200°C | ASTME831 | 1.5E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:0to100°C | ASTME831 | 7.6E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:100to200°C | ASTME831 | 1.2E-04 | cm/cm/°C |
Linear thermal expansion coefficient | TD:100to200°C | ASTME831 | 1.2E-04 | cm/cm/°C |
Melting temperature | | ISO11357-3 | 327 | °C |
Melting temperature | | ASTMD570 | 327 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | 1.60mm | ASTMD149 | 20 | KV/mm |
Dielectric Constant | 60Hz | ASTMD150 | 3.80 | |
Dielectric Constant | 1MHz | ASTMD150 | 3.60 | |
Volume Resistivity | | ASTMD257 | 2E+16 | ohms·cm |
High Voltage Arc Tracking Rate | HVTR | UL746 | 14.0 | mm/min |
Comparative Tracking Index | CTI | UL746 | 600 | V |
Dissipation Factor? | 60Hz | ASTMD150 | 4E-03 | |
Dissipation Factor? | 1MHz | ASTMD150 | 0.012 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod impact strength | 23°C | ISO180/1U | 59 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 67 | kJ/m² |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Light Transmittance | 1070nm:1.60mm | ASTMD1003 | >20 | % |
Light Transmittance | 940nm:1.60mm | ASTMD1003 | >20 | % |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 3.2mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.