Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Across Flow | ISO 294-4 | 1.1 | % |
| Modeling Shrinkage | 流量 | ISO 294-4 | 0.35 | % |
| Moisture Absorption | 24 hr, 23°C | ISO 62 | 0.75 | % |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 5.4 | % |
| Moisture Absorption | Equilibrium, 23°C, 50% RH | ISO 62 | 1.6 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break, 23°C | ISO 527-2/1A | 210 | Mpa |
| Tensile Strain | Break, 23°C | ISO 527-2 | 3.0 | % |
| Tensile Modulus | 23°C | ISO 527-2/1A | 11400 | Mpa |
| Flexural Modulus | 23°C | ASTM D790 | 9800 | Mpa |
| Flexural Modulus | 23°C | ISO 178 | 9500 | Mpa |
| Flexural Strength | 23°C | ASTM D790, ISO 178 | 290 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ASTM D648, ISO 75-2/Af | 255 | °C |
| Melting temperature | | ISO 11357-3 | 263 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | 2.00 mm | IEC 60243-1 | 34 | KV/mm |
| Dissipation Factor? | | IEC 60250 | 0.010 | |
| Surface Resistivity | | IEC 60093 | 6.0E+15 | ohms |
| Volume Resistivity | | IEC 60093 | 1.0E+15 | ohms·cm |
| Relative Permittivity | | IEC 60250 | 3.70 | |
| Comparative Tracking Index | Solution A | IEC 60112 | 400 | V |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature | | | 80 | °C |
| Suggested Max Moisture | | | 0.20 | % |
| Mold Temperature | | | 70 到 100 | °C |
| Rear Temperature | | | 270 到 280 | °C |
| Middle Temperature | | | 275 到 285 | °C |
| Front Temperature | | | 280 到 290 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 90 | kJ/m² |
| Notched Izod impact strength | 23°C | ISO 180/1U | 80 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Index | | ISO 4589-2 | 23 | % |
| Flame Rating | 0.8 mm | UL 94 | HB | |
| Flame Rating | 1.6 mm | UL 94 | HB | |
| Flame Rating | 3.2 mm | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.