PA66 TECHNYL® A218V35 SOLVAY FRANCE
40
- Unit Price:
- $3570 USD/MT
- Packaging Specification:
- 25KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Moisture Absorption | 23 ℃,24hr | ISO 62 | 干燥|0.75 | % |
Saturation | ISO 622 | 干燥|5.5 | % | |
Equilibrium | ISO 622 | 干燥|1.4 | % | |
Viscosity number | ISO 307,1157,16282 | 干燥|142 | cm³/g |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Tensile Stress | Break | ISO 527-2/1A | 干燥|210 | Mpa |
Break | ISO 527-2/1A | 调节后|150 | Mpa | |
Break | ISO 527-22 | 干燥|190 | Mpa | |
Break | ISO 527-22 | 调节后|145 | Mpa | |
Tensile Strain | Break | ISO 527-2/1A2, ISO 527-22 | 干燥|3.0 | % |
Break | ISO 527-2/1A2, ISO 527-22 | 调节后|4.0 | % | |
Tensile Modulus | ISO 527-2/1A2 ISO 527-22 | 干燥|11400 | Mpa | |
ISO 527-2/1A2 ISO 527-22 | 调节后|8700 | Mpa | ||
Flexural Modulus | ISO 178 | 干燥|9500 | Mpa | |
ISO 178 | 调节后|6800 | Mpa | ||
Charpy Notched Impact Strength | -- | ISO 179/1eA | 干燥|14 | kJ/m² |
-- | ISO 179/1eA | 调节后|19 | kJ/m² | |
23℃ | ISO 179/1eA2 | 干燥|13.5 | kJ/m² | |
23℃ | ISO 179/1eA2 | 调节后|18.5 | kJ/m² | |
-- | ISO 179/1eU | 干燥|95 | kJ/m² | |
-- | ISO 179/1eU | 调节后|100 | kJ/m² | |
23℃ | ISO 179/1eU2 | 干燥|95.0 | kJ/m² | |
23℃ | ISO 179/1eU2 | 调节后|100 | kJ/m² | |
Notched Izod Impact Strength | ISO 180/1A | 干燥|13 | kJ/m² | |
ISO 180/1A | 调节后|18 | kJ/m² |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Melting Temperature | -- | ISO 3146 | 干燥|263 | °C |
--3 | ISO 11357-32 | 干燥|260 | °C | |
Coefficient of Linear Thermal Expansion | Flow | ISO 11359-22 | 干燥|0.000022 | cm/cm/ ℃ |
Across Flow: 23 to 85℃ | ISO 11359-2 | 干燥|0.000022 | cm/cm/ ℃ |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|---|---|---|---|
Arc Resistance | IEC 60243-1 | 干燥|34 | KV/mm | |
IEC 60243-1 | 调节后|29 | KV/mm | ||
Surface Resistivity | -- | IEC 60093 | 干燥|6.0E+14 | Ohm |
-- | IEC 60093 | 调节后|1.0E+12 | Ohm | |
-- | IEC 600932 | 调节后|1.0E+12 | Ohm | |
Volume Resistivity | -- | IEC 60093 | 干燥|1.0E+15 | ohm.cm |
-- | IEC 60093 | 调节后|1.0E+13 | ohm.cm | |
-- | IEC 600932 | 干燥|1.0E+13 | ohm.m | |
-- | IEC 600932 | 调节后|1.0E+11 | ohm.m | |
Dissipation Factor? | -- | IEC 60250 | 干燥|0.010 | |
-- | IEC 60250 | 调节后|0.11 | ||
100 Hz | IEC 60250 2 | 干燥|0.010 | ||
100 Hz | IEC 60250 2 | 调节后|0.15 | ||
1 MHz | IEC 60250 2 | 干燥|0.010 | ||
1 MHz | IEC 60250 2 | 调节后|0.11 | ||
Relative Permittivity | -- | IEC 60250 | 干燥|3.70 | |
-- | IEC 60250 | 调节后|4.00 | ||
100 Hz | IEC 60250 2 | 干燥|4.00 | ||
100 Hz | IEC 60250 2 | 调节后|9.00 | ||
1 MHz | IEC 60250 2 | 干燥|3.70 | ||
1 MHz | IEC 60250 2 | 调节后|4.00 | ||
Comparative Tracking Index | Solution A | IEC 60112 | 干燥|450 | V |
Solution A | IEC 60112 | 调节后|450 | V | |
-- | IEC 601122 | 调节后|450 | V |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.