PA66 A60G1V30 SOLVAY SHANGHAI
107
- Unit Price:
- $5604 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Outdoor applicability | 全部 | UL 746C | f1 | |
| Shrinkage rate | Across Flow | ISO 294-4 | 1.0 | % |
| 流量 | ISO 294-4 | 0.35 | % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 0.73 | % |
| Saturation, 23°C | ISO 62 | 4.3 | % | |
| Equilibrium, 23°C, 50% RH | ISO 62 | 1.8 | % | |
| 1% weight loss (TGA) | NF F16-101 | I3 | ||
| density | ISO 1183/A | 1.46 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Break, 23°C | ASTM D638 | 140 | Mpa |
| Break, 23°C | ISO 527-2/1A | 150 | Mpa | |
| Tensile modulus | 23°C | ISO 527-2/1A | 10200 | Mpa |
| elongation | Break, 23°C | ASTM D638 | 3.0 | % |
| Break, 23°C | ISO 527-2 | 2.3 | % | |
| Bending modulus | 23°C | ASTM D790, ISO 178 | 10000 | Mpa |
| bending strength | 23°C | ASTM D790 | 225 | Mpa |
| 23°C | ISO 178 | 255 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/Af | 245 | °C |
| Melting temperature | ISO 11357-3 | 263 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 0.800 mm | IEC 60243-1 | 38 | KV/mm |
| Leakage Trace Index | Solution A | IEC 60112 | 600 | V |
| Volume resistivity | IEC 60093 | 6.0E+14 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| Suggested maximum moisture content | 0.20 | % | ||
| Mold temperature | 60 到 90 | °C | ||
| Temperature at the rear of the barrel | 265 到 275 | °C | ||
| Temperature in the middle of the barrel | 265 到 275 | °C | ||
| Temperature at the front of the material cylinder | 270 到 280 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 9.5 | kJ/m² |
| 23°C | ISO 179/1eA | 10 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 85 | J/m |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 60 | kJ/m² |
| 23°C | ISO 179/1eU | 60 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 0.8 mm | IEC 60695-2-12 | 960 | °C |
| 1.6 mm | IEC 60695-2-12 | 960 | °C | |
| 3.2 mm | IEC 60695-2-12 | 960 | °C | |
| Extreme Oxygen Index | ISO 4589-2 | 33 | % | |
| Hot filament ignition temperature | 0.8 mm | IEC 60695-2-13 | 775 | °C |
| European Railways Certifications | R22 | EN 45545-2 | HL3 | |
| R23 | EN 45545-2 | HL3 | ||
| UL flame retardant rating | 0.8 mm | UL 94 | V-0 | |
| 1.6 mm | UL 94 | V-0 5VA | ||
| 3.2 mm | UL 94 | V-0 5VA |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.