Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Index | | ISO 4589 | 29 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength (Break) | | ISO 527-2 | 85/50 | Mpa |
| Tensile Elongation?(Break) | RH0/RH50 | ISO 527-2 | 20/＞50 | % |
| Tensile Modulus | RH0/RH50 | ISO 527-2 | 3200/1600 | Mpa |
| Charpy Notched Impact Strength | RH0/RH50 | ISO 179/1eA | 5/15 | kJ/m² |
| Charpy Unnotched Impact Strength | | ISO 179/1eU | NB/NB | kJ/m² |
| IZOD Notch Impact Strength | RH0/RH50 | ISO 180/1A（93） | 5/12 | kJ/m² |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.80MPa | ISO 75-2 | 75 | °C |
| Melting Temperature | | ISO 3146-C | 260 | °C |
| Linear expansion coefficient | 23-85℃ | ASTM E-831 | 7 | 10-5·K-1 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Comparative Tracking Index | RH0/RH50 | IEC 112 | 600 | V |
| Dielectric Constant | RH0/RH50,1MHz | IEC 250 | 2.9/3.2 | |
| Dielectric Strength | RH0/RH50 | IEC 243 | 27/26 | KV/mm |
| Volume Resistivity | | IEC 93 | 1015/1013 | Ω.cm |
| Dissipation Factor | RH0/RH50,1MHz | IEC 250 | 0.03/0.08 | |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Hygroscopicity | 23℃，24hr | ISO 62 | 1.2 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.