Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 23°C,24hr | ISO62 | 0.80 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break,23°C | ISO527-2/1A | 190 | Mpa |
| Tensile Strain | Break,23°C | ISO527-2 | 3.0 | % |
| Tensile Strength | Yield,23°C | ASTMD638 | 190 | Mpa |
| Flexural Stress | 23°C | ISO178 | 275 | Mpa |
| Tensile Modulus | 23°C | ISO527-2/1A | 10000 | Mpa |
| Tensile Elongation | Break,23°C | ASTMD638 | 3.5 | % |
| Flexural Modulus | 23°C | ASTMD790 | 9000 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 9000 | Mpa |
| Flexural Strength | 23°C | ASTMD790 | 270 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/Bf | 260 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 250 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/Af | 255 | °C |
| Melting temperature | | ISO11357-3 | 262 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Relative Permittivity | | IEC60250 | 3.70 | |
| Comparative Tracking Index | SolutionA | IEC60112 | 600 | V |
| Surface Resistivity | | IEC60093 | 1E+15 | ohms |
| Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
| Dielectric Strength | 2.00mm | IEC60243-1 | 35 | KV/mm |
| Dissipation Factor? | | IEC60250 | 0.020 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod impact strength | 23°C | ISO180/1U | 75 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 85 | kJ/m² |
| Unnotched Izod Impact Strength | 23°C | ASTMD256 | 95.0 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| UL flame retardant rating | 3.2mm | UL94 | HB | |
| GlowWireFlammability | 1.6mm | IEC60695-2-12 | 700 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.