Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 23°C,24hr | ISO62 | 1.1 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield,23°C | ISO527-2/1A | 47.0 | Mpa |
Tensile Stress | Break,23°C | ISO527-2/1A | 44.0 | Mpa |
Tensile Strain | Yield,23°C | ISO527-2 | 20 | % |
Flexural Stress | 23°C | ISO178 | 70.0 | Mpa |
Tensile Modulus | 23°C | ISO527-2/1A | 1900 | Mpa |
Tensile Elongation | Break,23°C | ASTMD638 | 80 | % |
Flexural Modulus | 23°C | ASTMD790 | 1800 | Mpa |
Flexural Modulus | 23°C | ISO178 | 1800 | Mpa |
Flexural Strength | 23°C | ASTMD790 | 70.0 | Mpa |
Tensile Strength | Yield,23°C | ASTMD638 | 50.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melting temperature | | ISO11357-3 | 263 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 200 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 63.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/Af | 65.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC60093 | 1E+15 | ohms |
Volume Resistivity | | IEC60093 | 1E+15 | ohms·cm |
Dielectric Strength | 2.00mm | IEC60243-1 | 30 | KV/mm |
Relative Permittivity | | IEC60250 | 3.20 | |
Comparative Tracking Index | SolutionA | IEC60112 | 575 | V |
Comparative Tracking Index | SolutionB | IEC60112 | 450 | V |
Dissipation Factor? | | IEC60250 | 0.020 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 16 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | NoBreak | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.6mm | UL94 | HB | |
Oxygen Index | | ISO4589-2 | 25 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.