Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | | 1.0to2.0 | % |
| Melt Mass-Flow Rate | 230°C/2.16kg | ISO1133 | 45 | g/10min |
| Density | | ISO1183 | 0.910 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | 屈服 | ISO527-2/50 | 34.0 | Mpa |
| Tensile Strain | 屈服 | ISO527-2/50 | 6.0 | % |
| Tensile Modulus | | ISO527-2/1 | 1750 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 116 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Multi-Axial Instrumented Impact Energy | -20°C,TotalPenetrationEnergy | ISO6603-2 | 10.0 | J |
| Multi-Axial Instrumented Impact Energy | 0°C,TotalPenetrationEnergy | ISO6603-2 | 10.0 | J |
| Charpy Notched Impact Strength | -20°C | ISO179/1eA | 2.5 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 4.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R级 | ISO2039-2 | 100 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.