PP DOWLEX™ 2035G STYRON US
89
- Unit Price:
- $1525 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 6.0 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Gardner Impact | 23um，Cast Film | ASTM D-1709A | 120 | g |
| Tensile Elongation (Break MD) | 23um，Cast Film | ASTM D-882 | 520 | % |
| Tensile Elongation (Break TD) | 23um，Cast Film | ASTM D-882 | 690 | % |
| Elmendorf Tear Strength (TD) | 23um，Cast Film | ASTM D-1922 | 490 | |
| Elmendorf Tear Strength (MD) | 23um，Cast Film | ASTM D-1922 | 250 | g |
| Tensile Strength (Break TD) | 23um，Cast Film | ASTM D-882 | 20 | Mpa |
| Tensile Strength (Break TD) | 23um，Cast Film | ASTM D-882 | 26 | Mpa |
| Tensile Strength (Yield TD) | 23um，Cast Film | ASTM D-882 | 7 | Mpa |
| Tensile Strength (Yield MD) | 23um，Cast Film | ASTM D-882 | 7 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ISO 306/A | 97 | °C | |
| Vicat Softening Temperature | ISO306/A | 97.0 | °C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 薄膜拉伸性能-货盘上的负载3 | ASTMD4649 | 13000 | g | |
| Tensile Elongation | ASTMD4649 | 47 | % | |
| Tensile Elongation (Break) | ASTMD4649 | 340 | % | |
| Film Thickness - Tested) | 23 | µm | ||
| Tensile Strength | MD:Yield,23μm,挤塑薄膜 | ASTMD882 | 7.00 | Mpa |
| TD:Yield,23μm,挤塑薄膜 | ASTMD882 | 7.00 | Mpa | |
| MD:Break,23μm,挤塑薄膜 | ASTMD882 | 26.0 | Mpa | |
| TD:Break,23μm,挤塑薄膜 | ASTMD882 | 20.0 | Mpa | |
| Tensile Elongation | MD:Break,23μm,挤塑薄膜 | ASTMD882 | 520 | % |
| TD:Break,23μm,挤塑薄膜 | ASTMD882 | 690 | % | |
| Gardner Impact | 23µm,铸造薄膜 | ASTMD1709A | 120 | g |
| Elmendorf Tear Strength | MD:23µm,铸造薄膜 | ASTMD1922 | 250 | g |
| TD:23µm,铸造薄膜 | ASTMD1922 | 490 | g |
| Processing | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt Temperature | 220-280 | °C |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Haze | 23um，Cast Film | ASTM D-1003 | 0.7 | % |
| Gloss | 20°，23um，Cast Film | ASTM D-2457 | 148 | |
| Haze | 23.0µm,铸造薄膜 | ASTMD1003 | 0.70 | % |
| Gloss | 20°,23.0µm,铸造薄膜 | ASTMD2457 | 148 |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D-792 | 0.919 | g/m3 | |
| Film Thickness | 23 | um | ||
| Melt Mass-Flow Rate | 190℃/2.16kg | ISO 1133 | 6 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.