Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | % | ISO 294-4 | 0.9 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore D,Injection成型 | | ISO 868 | 58 |
| Tensile Modulus | | MPa | ISO 527-2 | |
| Tensile Modulus | Injection成型 | MPa | ISO 527-2/1 | 1400 |
| Tensile Strength(Yield) | | MPa | ISO 527-2 | 15.7 |
| Tensile Strength(Yield) | Injection成型 | MPa | ISO 527-2/50 | |
| Notched Impact Strength | -40℃ | KJ/m | ISO 180/1A | |
| Notched Impact Strength | -20℃ | KJ/m | ISO 180/1A | 37 |
| Tensile Strain(Yield) | Injection成型 | % | ISO 527-2/50 | |
| Tensile Strain(Yield) | | % | ISO 527-2 | 4.2 |
| Charpy Notched Impact Strength | -30℃ | KJ/m | ISO 179/1eA | |
| Nominal Tensile Strain | | % | ISO 527-2 | ＞50 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPA，Unannealed | ℃ | ISO 75-2/B | 88 |
| Deflection Temperature Under Load? | 1.8MPA，Unannealed | ℃ | ISO 75-2/A | 53 |
| Vicat Softening Temperature | | ℃ | ISO 306/A50 | 129 |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 230℃/2.16 kg | g/10 min | ISO 1133 | |
| Melt index | 230°C/5.0 kg | g/10 min | ISO 1133 | |
| Density | | g/cm | ISO 1183 | 1 |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | 流：-30 to 70°C | cm/cm/℃ | ISO 11359-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.