Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | % | ISO 294-4 | 1.1 |
| Modeling Shrinkage | 90°C, 2 hr | % | ISO 294-4 | 0.15 |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | -30℃ | J/m | ISO 180/1A | |
| Notched Izod Impact Strength | 23℃ | J/m | ISO 180/1A | 48 |
| Flexural Modulus | | MPa | ISO 178 | 880 |
| Tensile Strength(Yield) | | MPa | ISO 527-2/50 | |
| Charpy Notched Impact Strength | -30℃ | KJ/m | ISO 179/1eA | |
| Charpy Notched Impact Strength | -20℃ | KJ/m | ISO 179/1eA | |
| Charpy Notched Impact Strength | 23℃ | KJ/m | ISO 179/1eA | |
| Ball PressureTest | H 358/30 | MPa | ISO 2039-1 | 28 |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPA，Unannealed | ℃ | ISO 75-2/B | 74 |
| Vicat Softening Temperature | | ℃ | ISO 306/A50 | 121 |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt index | 230℃/2.16 kg | g/10 min | ISO 1133 | |
| Melt index | 230°C/5.0 kg | g/10 min | ISO 1133 | 55 |
| Density | | g/10 min | ISO 1183 | 0.94 |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear thermal expansion coefficient | 流：23 to 80°C | cm/cm/℃ | ISO 11359-2 | 0.000080 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.