Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 230°C/2.16kg | ISO1133 | 53 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ISO527-2/1 | 1680 | Mpa |
| Flexural Modulus | | ISO178 | 1660 | Mpa |
| Tensile Stress | Yield | ISO527-2/50 | 35.8 | Mpa |
| Tensile Strain | Yield | ISO527-2/50 | 7.7 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ISO306/A50 | 153 | °C |
| Melting temperature (DSC) | | ISO3146 | 162 | °C |
| Peak Crystallization Temperature? | DSC | ISO3146 | 124 | °C |
| 0.45MPa, Unannealed | | ISO75-2/B | 96.0 | °C |
| 1.8MPa, Unannealed | | ISO75-2/A | 52.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 2.6 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 2.3 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore D | ISO868 | 71 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.