Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 230°C/2.16kg | ASTMD1238 | 8.0 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO527-2/1 | 1290 | Mpa |
Tensile Elongation | Yield3 | ASTMD638 | 6.5 | % |
Tensile Elongation | Yield | ISO527-2/50 | 5.6 | % |
Flexural Modulus | 1%Secant4 | ASTMD790A | 1140 | Mpa |
Flexural Modulus | 1%Secant5 | ASTMD790B | 1280 | Mpa |
Flexural Modulus | --6 | ISO178 | 1190 | Mpa |
Tensile Strength | Yield3 | ASTMD638 | 23.9 | Mpa |
Tensile Strength | Yield | ISO527-2/50 | 23.1 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 90.2 | °C |
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/Bf | 85.3 | °C |
Deflection Temperature Under Load? | 0.45MPa,Annealed | ASTMD648 | 114 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 50.9 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Gardner Impact | -29°C,3.18mm | ASTMD5420 | 28.1 | J |
Charpy Notched Impact Strength | -30°C | ISO179/1eA | 4.3 | kJ/m² |
Charpy Notched Impact Strength | -20°C | ISO179/1eA | 5.4 | kJ/m² |
Charpy Notched Impact Strength | 0°C | ISO179/1eA | 6.7 | kJ/m² |
Charpy Notched Impact Strength | 23°C | ISO179/1eA | 14 | kJ/m² |
Notched Izod Impact Strength | 23°C | ASTMD256A | 280 | J/m |
Notched Izod Impact Strength | -40°C | ISO180/1A | 4.0 | kJ/m² |
Notched Izod Impact Strength | -18°C | ISO180/1A | 5.7 | kJ/m² |
Notched Izod Impact Strength | 23°C | ISO180/1A | 13 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | | ASTMD785 | 89 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.