Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | | ASTMD1238 | 3.0 | g/10min |
| Apparent Density | | ASTMD1895 | 0.66 | g/cm³ |
| Modeling Shrinkage | MD | ASTMD955 | 0.20到0.50 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | Yield | ASTMD638 | 65.5 | Mpa |
| Tensile Elongation | Yield | ASTMD638 | 3.0 | % |
| Flexural Modulus | | ASTMD790 | 3380 | Mpa |
| Flexural Strength | Yield | ASTMD790 | 96.5 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 68.9 | °C |
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ASTMD648 | 76.7 | °C |
| Specific Heat | 20°C | ASTMC351 | 1340 | J/kg/°C |
| Thermal Conductivity | | ASTMC177 | 0.25 | W/m/K |
| Linear thermal expansion coefficient | MD：20to80°C | ASTMD696 | 6.7E-05 | cm/cm/°C |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Oxygen Transmission Rate | 23°C,100%RH | ASTMD3985 | 0.31 | cm³·mm/m²/atm/24hr |
| Water Vapor Transmission Rate | | ASTMF1249 | 2.0 | g·mm/m²/atm/24hr |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M-Scale | ASTMD785 | 60 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| The Yellow Index | 0.254mm | ASTMD1925 | 2.5 | YI |
| Haze | 254µm | ASTMD1003 | 2.7 | % |
| Transmittance | 254µm | ASTMD1003 | 92.5 | % |
| Gloss | 60°,254µm | ASTMD2457 | 120 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.