Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1.04 | |
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Volume flow Rate | 230°C/2.16kg | ISO1133 | 9.00 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO527-2/1A/1 | 1900 | Mpa |
Tensile Stress | Yield | ISO527-2/1A/50 | 22.0 | Mpa |
Tensile Strain | Yield | ISO527-2/1A/50 | 3.0 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/Bf | 108 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/Af | 58.0 | °C |
RTIElec | 1.5mm | UL746 | 65.0 | °C |
RTIElec | 3.0mm | UL746 | 65.0 | °C |
Evolution Calendar intelligent importer | 1.5mm | UL746 | 65.0 | °C |
Evolution Calendar intelligent importer | 3.0mm | UL746 | 65.0 | °C |
RTIStr | 1.5mm | UL746 | 65.0 | °C |
RTIStr | 3.0mm | UL746 | 65.0 | °C |
Vicat Softening Temperature | -- | ISO306/A50 | 150 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 72.0 | °C |
Ball PressureTest | 125°C | IEC60695-10-2 | Pass | |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
High Amp Arc Ignition | 1.5mm | UL746 | PLC0 | |
High Amp Arc Ignition | 3.0mm | UL746 | PLC0 | |
Hot-wire Ignition | 1.5mm | UL746 | PLC3 | |
Hot-wire Ignition | 3.0mm | UL746 | PLC0 | |
Comparative Tracking Index | | IEC60112 | 600 | V |
Surface Resistivity | | IEC60093 | >1.0E+15 | ohms |
Volume Resistivity | | IEC60093 | >1.0E+13 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 11 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 37 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5mm | UL94 | V-0 | |
UL flame retardant rating | 3.0mm | UL94 | V-0 | |
UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | V-0 | |
UL flame retardant rating | 3.0mm | IEC60695-11-10,-20 | V-0 | |
Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | 960 | °C |
Glow Wire Flammability Index | 3.0mm | IEC60695-2-12 | 960 | °C |
Oxygen Index | | ISO4589-2 | 36 | % |
Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 725 | °C |
Glow Wire Ignition Temperature | 3.0mm | IEC60695-2-13 | 725 | °C |
Burning Rate | 1.50mm,自动灭火 | ISO3795 | 0.0 | mm/min |
Burning Rate | 3.00mm,自动灭火 | ISO3795 | 0.0 | mm/min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.