Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Apparent Density | | g/cm³ | 0.52到0.53 | |
| -- | | | 0.900到0.904 | |
| -- | | g/cm³ | 0.900 | |
| 23℃ | | g/cm³ | 0.891到0.910 | |
| 23℃ | | % | 1.5 | |
| Flow:23℃ | | mm/mm | 0.330到0.457 | |
| Spiral Flow | | mm | 500.38到800.10 | |
| 230°C/2.16kg | | g/10min | 0.25到38 | |
| 230°C/2.16kg | | g/10min | 0.20到28 | |
| Melt Volume flow Rate | 230°C/2.16kg | ISO 527-2/5, ISO 527-2/50 | 0.01到0.25 | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus | 23℃ | MPa | 737.93到827.59 | |
| 23℃ | | MPa | 793.1到1303.45 | |
| 23℃ | | MPa | 572.41到1255.17 | |
| 23℃ | | MPa | 765.52到1268.97 | |
| 23℃ | | MPa | 889.66到1200.0 | |
| Break,23℃ | | % | 78到510 | |
| Break,23℃ | | MPa | 19.31到44.34 | |
| Break,23℃ | | % | 46到510 | |
| Break,23℃ | | MPa | 14.48到40.0 | |
| Yield,23℃ | | % | 10到16 | |
| Yield,23℃ | | MPa | 24.41到30.48 | |
| Yield,23℃ | | % | 6.0到28 | |
| Yield,23℃ | | MPa | 19.59到31.38 | |
| Tensile Modulus | 摩擦系数 | | 0.15到1.0 | |
| Flexural Stress | 23℃ | MPa | 6.5到25.03 | |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| 0.45MPa, Unannealed | | °C | 72到100 | |
| 0.45MPa, Unannealed | | °C | 54到85 | |
| 1.8MPa, Unannealed | | °C | 45到96 | |
| 1.8MPa, Unannealed | | °C | 48到55 | |
| -- | | °C | 127到150 | |
| -- | | °C | 65到136 | |
| -- | | °C | 125到148 | |
| -- | | °C | 125到150 | |
| -- | | °C | 124到139 | |
| -- | | °C | 132到150 | |
| -- | | °C | 140到150 | |
| Film | Test Condition | Test Method | Test Result | Unit |
|---|
| Film Thickness - Tested) | | | 2.0到3.1 | |
| Peak Melting Temperature | | °C | 105到115 | |
| MD:Break | | MPa | 20.34到40.55 | |
| MD:Break | | % | 490到760 | |
| MD: Yield | | MPa | 18.0到22.62 | |
| 23℃ | | MPa | 25.03到42.48 | |
| 23℃ | | MPa | 190.34到800.0 | |
| MD | | MPa | 344.83到793.1 | |
| Break,23℃ | | % | 500到760 | |
| Break,23℃ | | MPa | 29.03到39.59 | |
| Instrumented Dart Impact | 23℃ | J | 0.54到16.45 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Gardner Impact | 23℃ | N.m | 1831.86到2831.86 | |
| Unnotched Izod Impact Strength | 23℃ | J/m | 0.013到0.024 | |
| Charpy Unnotched Impact Strength | 23℃ | kJ/m² | 1.114到45.037 | |
| 23℃ | | J/m | 0.009到0.028 | |
| 23℃ | | kJ/m² | 0.744到2.089 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | 23℃ | | 58到68 | |
| Ball Indentation Hardness | | MPa | 44.83到60.0 | |
| Shore Hardness | 23℃ | | 75到98 | |
| 23℃ | | | 79到100 | |
| 23℃ | | | 52到80 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | | % | 0.40到17 | |
| Gloss | | | 79到132 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.