PP SABIC® 1128NK SABIC SAUDI

Unit Price:
$1402 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Melt Mass-Flow Rate	230°C/2.16kg	ISO1133	11	g/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Coefficient of Friction		DIN53375	0.18
Tensile Modulus		ISO527-2/1	1500	Mpa
Flexural Modulus	流量:0.0500mm,铸造薄膜	DIN53121	700	Mpa
Flexural Modulus	Flexural Modulus	Across Flow:0.0500mm,铸造薄膜	DIN53121	670	Mpa
Tensile Stress	Yield	ISO527-2/50	35.0	Mpa
Tensile Strain	Yield	ISO527-2/50	9.0	%
Tensile Strain	Tensile Strain	Break	ISO527-2/50	>50	%

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,Unannealed	ISO75-2/B	85.0	°C
Vicat Softening Temperature		ISO306/A50	154	°C
Melting temperature (DSC)		ISO3146	163	°C

Film	Test Condition	Test Method	Test Result	Unit
Film Thickness - Tested)			50	µm
Tensile Elongation	MD:Break,50μm,铸造薄膜	DIN53455	680	%
Tensile Elongation	Tensile Elongation	TD:Break,50μm,铸造薄膜	DIN53455	720	%
Gardner Impact	50µm,铸造薄膜	ASTMD1709	280	g

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness	H358/30	ISO2039-1	76.0	Mpa

optical performance	Test Condition	Test Method	Test Result	Unit
Gloss	20°,50.0µm,铸造薄膜	ISO2813	100
Haze	1000μm,Injection	ASTMD1003	2.7	%

Supplementary information	Test Condition	Test Method	Test Result	Unit
Tearing Strength	MD:50.0µm	DIN53455	42.0	Mpa
Tearing Strength	Tearing Strength	TD:50.0µm	DIN53455	38.0	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.