PBT LEXAN™ 310SEO-7001 SABIC INNOVATIVE THAILAND

Unit Price:
$4223 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant
Application Areas:Electrical field Electronic field Industrial applications switch Shell
Color:--
Grade:Injection grade

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow 2	内部方法	1.1 到 1.8	%
	Modeling Shrinkage	Flow : 0.750 to 2.30 mm	内部方法	0.90 到 1.6	%
		Modeling Shrinkage	Flow : 3.20 mm	内部方法	1.5 到 2.3	%
			Modeling Shrinkage	Flow : 2.30 to 4.60 mm	内部方法	1.5 到 2.3	%
				Modeling Shrinkage	Across Flow 2	内部方法	0.90 到 1.9	%
					Modeling Shrinkage	Across Flow : 0.750 to 2.30 mm	内部方法	1.0 到 1.7	%
					Modeling Shrinkage	Modeling Shrinkage	Across Flow : 2.30 to 4.60 mm	内部方法	1.6 到 2.4	%
Moisture Absorption	Saturation, 23°C	ISO 62	0.36	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.080	%
Specific Volume		ASTM D792	0.710	cm³/g
Melt Mass-Flow Rate	250°C/2.16 kg	ASTM D1238	8.6	g/10 min
Melt Volume flow Rate	250°C/2.16 kg	ISO 1133	8.00	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Taber Abrasion Resistance	1000 Cycles, 1000 g, CS-17 Wheel	内部方法	19.0	mg
Tensile Modulus	-- 3	ASTM D638	2820	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	2800	Mpa
Tensile Elongation	Yield 4	ASTM D638	5.0	%
	Tensile Elongation	Yield	ISO 527-2/50	5.0	%
		Tensile Elongation	Break 4	ASTM D638	18	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2/50	18	%
Flexural Modulus	50.0 mm Span 5	ASTM D790	2620	Mpa
Flexural Modulus	Flexural Modulus	-- 6	ISO 178	2600	Mpa
Tensile Strength	Yield 4	ASTM D638	58.0	Mpa
	Tensile Strength	Yield	ISO 527-2/50	58.0	Mpa
		Tensile Strength	Break 4	ASTM D638	52.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2/50	40.0	Mpa
Flexural Stress	-- 6, 7	ISO 178	90.0	Mpa
Flexural Stress	Flexural Stress	Yield, 50.0 mm Span 5	ASTM D790	101	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature	--	ASTM D152511, ISO 306/B50, ISO 306/B120	170	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO 306/A50	212	°C
Linear thermal expansion coefficient	Flow : -40 to 40°C	ASTM E831	7.9E-5	cm/cm/°C
	Linear thermal expansion coefficient	Flow : 60 to 138°C	ASTM E831	1.3E-4	cm/cm/°C
		Linear thermal expansion coefficient	Flow : -40 to 40°C	ISO 11359-2	7.6E-5	cm/cm/°C
			Linear thermal expansion coefficient	Flow : 23 to 60°C	ISO 11359-2	1.0E-4	cm/cm/°C
				Linear thermal expansion coefficient	Across Flow : -40 to 40°C	ASTM E831	7.9E-5	cm/cm/°C
					Linear thermal expansion coefficient	Across Flow : -40°C	ISO 11359-2	7.3E-5	cm/cm/°C
					Linear thermal expansion coefficient	Linear thermal expansion coefficient	Across Flow : 23 to 60°C	ISO 11359-2	1.0E-4	cm/cm/°C
Thermal Conductivity		ISO 8302	0.24	W/m/K
RTI		UL 746	140	°C
RTI Imp		UL 746	120	°C
RTI Elec		UL 746	120	°C
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	162	°C
	Deflection Temperature Under Load?	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 10	ISO 75-2/Be	150	°C
		Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	74.0	°C
			Deflection Temperature Under Load?	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	71.0	°C
				Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 10	ISO 75-2/Ae	60.0	°C
				Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 9	ISO 75-2/Af	73.0	°C
Ball PressureTest	123 to 127°C	IEC 60695-10-2	通过

Electrical performance	Test Condition	Test Method	Test Result	Unit
Relative Permittivity	50 Hz	IEC 60250	2.90
	Relative Permittivity	60 Hz	IEC 60250	2.90
		Relative Permittivity	100 Hz	IEC 60250	3.10
		Relative Permittivity	Relative Permittivity	1 MHz	IEC 60250	2.80
Comparative Tracking Index	--	IEC 60112	175	V
Comparative Tracking Index	Comparative Tracking Index	Solution B	IEC 60112	100	V
Dielectric Strength	1.60 mm, in Oil	ASTM D149	24	KV/mm
	Dielectric Strength	3.20 mm, in Air	ASTM D149	18	KV/mm
		Dielectric Strength	0.800 mm, in Oil	IEC 60243-1	35	KV/mm
			Dielectric Strength	1.00 mm 12	IEC 60243-1	18	KV/mm
				Dielectric Strength	1.60 mm, in Oil	IEC 60243-1	25	KV/mm
				Dielectric Strength	Dielectric Strength	3.20 mm, in Oil	IEC 60243-1	17	KV/mm
Surface Resistivity		IEC 60093	> 1.0E+15	ohms
Volume Resistivity		IEC 60093	> 1.0E+15	ohms·cm
Dissipation Factor?	50 Hz	IEC 60250	1.0E-3
	Dissipation Factor?	60 Hz	IEC 60250	1.0E-3
		Dissipation Factor?	100 Hz	IEC 60250	2.0E-3
		Dissipation Factor?	Dissipation Factor?	1 MHz	IEC 60250	0.013
Comparative Tracking Index		UL 746	PLC 3
Hot-wire Ignition		UL 746	PLC 2
High Voltage Arc Tracking Rate		UL 746	PLC 4
Arc Resistance		ASTM D495	PLC 6
High Amp Arc Ignition		UL 746	PLC 0
High Voltage Arc Tracking Rate		UL 746	PLC 6

Injection	Test Result	Unit
Drying Temperature	120	°C
Suggested Max Moisture	0.020	%
Processing (Melt) Temp	245 到 260	°C
Mold Temperature	50 到 75	°C
Drying Time	3.0 到 4.0	hr
Suggested Shot Size	40 到 80	%
Rear Temperature	230 到 250	°C
Middle Temperature	240 到 255	°C
Front Temperature	245 到 260	°C
Nozzle Temperature	240 到 255	°C
Back Pressure	0.300 到 0.700	Mpa
Screw Speed	50 到 100	rpm
Vent Depth	0.013 到 0.025	mm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-30°C	ISO 179/1eU	无断裂
Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C	ISO 179/1eU	无断裂
Unnotched Izod Impact Strength	23°C	ASTM D4812, ISO 180/1U	无断裂
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	-30°C 9	ISO 180/1U	无断裂
Instrumented Dart Impact	23°C, Total Energy	ASTM D3763	200	J

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell Hardness	R -Sale	ISO 2039-2	120
Ball Indentation Hardness	H 358/30	ISO 2039-1	105	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
Flame Rating	0.71 mm	UL 94	V-0
Flame Rating	Flame Rating	3.0 mm	UL 94	5VA
Glow Wire Flammability Index	1.0 mm	IEC 60695-2-12	960	°C
Oxygen Index		ISO 4589-2	30	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.