Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | TD | ISO294-4 | 0.87 | % |
Modeling Shrinkage | MD | ISO294-4 | 0.30 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Flexural Stress | 23°C | ISO178 | 300 | Mpa |
Tensile Modulus | 23°C | ISO527-2 | 11300 | Mpa |
Tensile Modulus | 150°C | ISO527-2 | 4200 | Mpa |
Flexural Modulus | 23°C | ISO178 | 10600 | Mpa |
Tensile Stress | Break,23°C | ISO527-2 | 200 | Mpa |
Tensile Stress | Break,150°C | ISO527-2 | 84.0 | Mpa |
Tensile Strain | Break,23°C | ISO527-2 | 2.9 | % |
Tensile Strain | Break,150°C | ISO527-2 | 6.7 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 260 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 240 | °C |
Melting temperature (DSC) | | ISO3146 | 260 | °C |
Linear thermal expansion coefficient | MD | | 1.4E-5to2.0E-5 | cm/cm/°C |
Linear thermal expansion coefficient | TD | | 8.0E-5to1.3E-4 | cm/cm/°C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Dielectric Strength | | IEC60243-1 | 48 | KV/mm |
Comparative Tracking Index | | IEC60112 | 250 | V |
Volume Resistivity | | IEC60093 | 3E+14 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO179 | 60 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 80 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.