AS(SAN) Stylac™ 767 ASAHI JAPAN

Unit Price:
$4989 USD/MT
Packaging Specification:
25KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

serv********

For more detailed information including pricing, customization, and shipping, please contact supplier.

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Density		ASTM D792/ISO 1183	1.08	kg·cm/cm(J/M)ft·lb/in
Melt Mass-Flow Rate		ASTM D1238/ISO 1133	12.5	g/10min

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD	ASTMD955	0.40到0.60	%
Melt Mass-Flow Rate	220°C/10.0kg	ISO1133	12	g/10min
Melt Volume flow Rate	220°C/10.0kg	ISO1133	13.0	cm3/10min

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Modulus		ISO178	3700	Mpa
Flexural Stress		ISO178	130	Mpa
Tensile Stress	Yield	ISO527-2/5	69.9	Mpa
Tensile Elongation?(Break)		ASTM D638/ISO 527	2.0	%
Tensile Strength		ASTM D638/ISO 527	72	kg/cm²(MPa)[Lb/in²]
Rockwell Hardness		ASTM D785	83
Flexural Modulus		ASTM D790/ISO 178	3430	kg/cm²(MPa)[Lb/in²]
Flexural Strength		ASTM D790/ISO 178	105	kg/cm²(MPa)[Lb/in²]
Izod notch impact strength		ASTM D256/ISO 179	15	kg·cm/cm(J/M)ft·lb/in

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Vicat Softening Temperature		ISO306/B	103	°C
Deflection Temperature Under Load?		ASTM D648/ISO 75	90	℃（℉）
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,Unannealed	ISO75-2/A	87.7	°C
Vicat Softening Temperature		ASTM D1525/ISO R306	110	℃（℉）
RTIElec		UL746	50.0	°C
Evolution Calendar intelligent importer		UL746	50.0	°C
RTI		UL746	50.0	°C
Ball PressureTest		EMAC	95	°C

Flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.