ULDPE ATTANE™ 4404G STYRON US
103
- Unit Price:
- $2261 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:optical performance High toughness High toughness and optica Certified by Canadian HPF
- Application Areas:packing film Mainly used for packaging
- Color:--
- Grade:Thin film grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 4.0 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Puncture intensity | 陶氏企业测试 | 17 | J/cm³ | |
| Tensile yield strength | TD | ASTM D-882 | 5 | Mpa |
| MD | ASTM D-882 | 7 | Mpa | |
| Tensile fracture strength | TD | ASTM D-882 | 32 | Mpa |
| MD | ASTM D-882 | 33 | Mpa | |
| Tensile strain at break | TD | ASTM D-882 | 714 | % |
| MD | ASTM D-882 | 664 | % | |
| Tensile modulus -2% Secant | TD | ASTM D-882 | 63 | Mpa |
| Tensile modulus -3% Secant | MD | ASTM D-882 | 63 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| vicat softening point | ASTM D-1525 | 71 | °C | |
| Vicat softening temperature | ASTMD1525 | 71.1 | °C | |
| Melting temperature (DSC) | 内部方法 | 124 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Falling hammer impact | 20µm | ASTMD1709B | >850 | g |
| 51µm | ASTMD1709B | >850 | g | |
| Elmondov tear strength | MD:20µm | ASTMD1922 | 330 | g |
| MD:51µm | ASTMD1922 | 960 | g | |
| TD:20µm | ASTMD1922 | 500 | g | |
| TD:51µm | ASTMD1922 | 1100 | g | |
| Oxygen permeability rate | 23°C,51µm | ASTMD3985 | 450 | cm³·mm/m²/atm/24hr |
| Water vapor permeability | 51µm | ASTMF1249 | 0.85 | g·mm/m²/atm/24hr |
| Carbon dioxide transmission rate | 23°C,50.8µm | 内部方法 | 2000 | cm³·mm/m²/atm/24hr |
| Membrane puncture resistance | 20µm | 内部方法 | 18.9 | J/cm³ |
| 51µm | 内部方法 | 17.5 | J/cm³ | |
| Secant modulus | 2%Secant,MD:20μm | ASTMD882 | 58.8 | Mpa |
| 2%Secant,MD:51μm | ASTMD882 | 62.6 | Mpa | |
| 2%Secant,TD:20μm | ASTMD882 | 64.7 | Mpa | |
| 2%Secant,TD:51μm | ASTMD882 | 63.0 | Mpa | |
| Tensile strength | MD:Yield,20μm | ASTMD882 | 7.00 | Mpa |
| MD:Yield,51μm | ASTMD882 | 6.76 | Mpa | |
| TD:Yield,20μm | ASTMD882 | 4.92 | Mpa | |
| TD:Yield,51μm | ASTMD882 | 6.34 | Mpa | |
| MD:Break,20μm | ASTMD882 | 36.9 | Mpa | |
| MD:Break,51μm | ASTMD882 | 32.6 | Mpa | |
| TD:Break,20μm | ASTMD882 | 29.1 | Mpa | |
| TD:Break,51μm | ASTMD882 | 32.4 | Mpa | |
| elongation | MD:Break,20μm | ASTMD882 | 500 | % |
| MD:Break,51μm | ASTMD882 | 660 | % | |
| TD:Break,20μm | ASTMD882 | 710 | % | |
| TD:Break,51μm | ASTMD882 | 710 | % |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| transparency | ASTM D-1746 | 99 | ||
| gloss | 45° | ASTM D-2457 | 90 | |
| Haze | ASTM D-1003 | 1.8 | % | |
| gloss | 45°,20.3µm | ASTMD2457 | 92 | |
| 45°,50.8µm | ASTMD2457 | 90 | ||
| transparency | 20.3µm | ASTMD1746 | 99.0 | |
| 50.8µm | ASTMD1746 | 99.0 | ||
| Haze | 20.3µm | ASTMD1003 | 0.60 | % |
| 50.8µm | ASTMD1003 | 1.8 | % |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | ASTM D1238 | 4 | g/10min | |
| density | ASTM D792 | 0.904 | g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.