Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 220°C/10.0 kg | ASTM D1238 | 21 | g/10 min |
Modeling Shrinkage - Flow | 23°C, 3.20 mm, Injection | ASTM D955 | 0.40 到 0.70 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Elongation | Yield, 23°C, 3.20 mm, Injection | ASTM D638 | > 5.0 | % |
Tensile Elongation | Break, 23°C, 3.20 mm, Injection | ASTM D638 | 15 | % |
Tensile Modulus | 23°C, 3.20 mm, Injection | ASTM D638 | 2050 | Mpa |
Flexural Modulus | 23°C, 3.20 mm, Injection | ASTM D790 | 2250 | Mpa |
Flexural Strength | 23°C, 3.20 mm, Injection | ASTM D790 | 71.0 | Mpa |
Tensile Strength | Yield, 23°C, 3.20 mm, Injection | ASTM D638 | 48.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | | ASTM D15257 | 89.0 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed, 6.40 mm, Injection | ASTM D648 | 81.0 | °C |
RTI | | UL 746 | 50.0 | °C |
RTI Imp | | UL 746 | 50.0 | °C |
RTI Elec | | UL 746 | 50.0 | °C |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | 80 到 90 | °C |
Processing (Melt) Temp | | | 190 到 220 | °C |
Mold Temperature | | | 40 到 60 | °C |
Drying Time | | | 2.0 到 4.0 | hr |
Rear Temperature | | | 180 到 200 | °C |
Middle Temperature | | | 190 到 210 | °C |
Front Temperature | | | 200 到 220 | °C |
Nozzle Temperature | | | 190 到 220 | °C |
Back Pressure | | | 29.4 到 58.8 | Mpa |
Screw Speed | | | 30 到 60 | rpm |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale, 23°C, Injection | ASTM D785 | 107 | |
optical performance | Test Condition | Test Method | Test Result | Unit |
---|
Haze | Injection | ASTM D1003 | 2.0 | % |
Transmittance | 3200 μm, Injection | ASTM D1003 | 90.0 | % |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 1.5 mm | UL 94 | HB | |
Flame Rating | 3.0 mm | UL 94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.