Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ASTM D792/ISO 1183 | 1080 | |
Modeling Shrinkage | | ASTM D955 | 0.4-0.7 | % |
Moisture Absorption 23℃/24H | | ASTM D570/ISO 62 | 0.7 | % |
Melt Mass-Flow Rate | | ASTM D1238/ISO 1133 | 17 | g/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ASTM D638/ISO 527 | 2000 | kg/cm²(MPa)[Lb/in²] |
Tensile Modulus | | MPa | ISO 527-1/-2 | 2000 |
Tensile Strength | | ASTM D638/ISO 527 | 48 | kg/cm²(MPa)[Lb/in²] |
Charpy Notched Impact Strength | +23℃ | KJ/m | ISO 179/1eA | |
Charpy Notched Impact Strength | -30℃ | KJ/m | ISO 179/1eA | 2 |
Charpy Unnotched Impact Strength | +23℃ | KJ/m | ISO 179/1eU | |
Charpy Unnotched Impact Strength | -30℃ | KJ/m | ISO 179/1eU | |
IZOD Notch Impact Strength | +23℃ | J/m | ASTM D-256 | |
Ball Indentation Hardness | | MPa | ISO 2039-1 | |
Fracture strain | 50mm/min | % | ISO 527-1/-2 | |
Tensile Stress (Yield) | 50mm/min | MPa | ISO 527-1/-2 | 48 |
Tensile Stress (Yield) | 50mm/min | % | ISO 527-1/-2 | |
Izod notch impact strength | | ASTM D256/ISO 179 | 120 | kg·cm/cm(J/M)ft·lb/in |
Izod notch impact strength | | ASTM D256/ISO 179 | 80 | kg·cm/cm(J/M)ft·lb/in |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Vicat Softening Temperature | VST/A/50 | ℃ | ISO 306 | 105 |
Vicat Softening Temperature | VST/B/50 | ℃ | ISO 306 | 93 |
Deflection Temperature Under Load? | 1.80MPa | ℃ | ISO 75-1/-2 | |
Deflection Temperature Under Load? | 0.45MPa | ℃ | ISO 75-1/-2 | 94 |
Deflection Temperature Under Load? | | ASTM D648/ISO 75 | 90 | ℃(℉) |
Vicat Softening Temperature | | ASTM D1525/ISO R306 | 105 | ℃(℉) |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | 100V | Ohm | IEC 60093 | 1E+15 |
Dielectric Constant | 100Hz | | IEC 60250 | |
Dielectric Constant | 1MHz | | IEC 60250 | 2.8 |
Volume Resistivity | 100V | | IEC 60093 | 1E+13 |
Dielectric Strength | | kV/mm | IEC 60243-1 | 34 |
Dissipation Factor? | 100Hz | E-4 | IEC 60250 | 160 |
Dissipation Factor? | 1MHz | E-4 | IEC 60250 | 140 |
Physical | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | equilibrium in water at 23°C | % | similar to ISO 62 | 0.7 |
Melt Volume flow Rate | | cm | ISO 1133 | |
Density | | Kg/m | ISO 1183 | 1080 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.