PA4T ForTii® K11 BK DSM HOLAND
199
- Unit Price:
- $7406 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 41.2MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Lubricity
- Application Areas:Electronic and electrical Automotive Applications
- Color:--
- Grade:--
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 1.3 | % |
| 流量 | ISO 294-4 | 0.40 | % | |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 2.1 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break | ISO 527-2 | 180 | Mpa |
| Break, 120°C | ISO 527-2 | 130 | Mpa | |
| Break, 160°C | ISO 527-2 | 90.0 | Mpa | |
| Break, 200°C | ISO 527-2 | 75.0 | Mpa | |
| Tensile strain | Break | ISO 527-2 | 2.0 | % |
| Break, 120°C | ISO 527-2 | 2.8 | % | |
| Break, 160°C | ISO 527-2 | 4.6 | % | |
| Break, 200°C | ISO 527-2 | 5.8 | % | |
| Tensile modulus | -- | ISO 527-2 | 11000 | Mpa |
| 120°C | ISO 527-2 | 8000 | Mpa | |
| 160°C | ISO 527-2 | 5000 | Mpa | |
| 200°C | ISO 527-2 | 5000 | Mpa | |
| Bending modulus | -- | ISO 178 | 10000 | Mpa |
| 160°C | ISO 178 | 5000 | Mpa | |
| 200°C | ISO 178 | 4000 | Mpa | |
| Bending stress | ISO 178 | 290 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | Flow | ASTM D696 | 3.0E-5 | cm/cm/°C |
| Across Flow | ASTM D696 | 5.0E-5 | cm/cm/°C | |
| Melting temperature 3 | ISO 11357-3 | 325 | °C | |
| Thermal Index - 5000 hr | IEC 60216 | 174 | °C | |
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 305 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC 60093 | > 1.0E+15 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 33 | KV/mm | |
| Relative permittivity | 100 Hz | IEC 60250 | 5.00 | |
| 1 MHz | IEC 60250 | 4.50 | ||
| 1.00 GHz | IEC 60250 | 3.90 | ||
| 10.0 GHz | IEC 60250 | 3.80 | ||
| Leakage Trace Index | IEC 60112 | 600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flammability level | 0.8 mm | IEC 60695-11-10, -20 | HB | |
| 1.5 mm | IEC 60695-11-10, -20 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.