Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Across Flow : 23°C, 72hr | ISO 2577 | 1.0 到 1.2 | % |
Modeling Shrinkage | 流量 : 23°C, 72hr | ISO 2577 | 1.0 到 1.2 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield | ISO 527-2/50 | 80.0 | Mpa |
Tensile Strain | Break | ISO 527-2/50 | 15 | % |
Tensile Modulus | | ISO 527-2/1 | 3600 | Mpa |
Flexural Modulus | | ISO 178 | 3300 | Mpa |
Flexural Stress | | ISO 178 | 120 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melting temperature | | ISO 11357-3 | 262 | °C |
Vicat Softening Temperature | | ISO 306/B50 | 215 | °C |
Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 200 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 75.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC 60093 | 1.0E+13 | ohms |
Volume Resistivity | | IEC 60093 | 1.0E+15 | ohms·cm |
Comparative Tracking Index | Solution A | IEC 60112 | 600 | V |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Drying Temperature | | | 75 到 85 | °C |
Processing (Melt) Temp | | | 260 到 280 | °C |
Mold Temperature | | | 60 到 80 | °C |
Drying Time | | | 2.0 到 4.0 | hr |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 80 kJ/m² | |
Notched Izod impact strength | 23°C | ISO 180/1U | 70 kJ/m² | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Glow Wire Flammability Index | 1.0 to 3.0 mm | IEC 60695-2-12 | 960 | °C |
Glow Wire Ignition Temperature | 1.0 to 3.0 mm | IEC 60695-2-13 | 750 | °C |
Burning Rate | | FMVSS 302 | < 100 | mm/min |
Flame Rating | 0.40 mm | UL 94 | V-0 | |
Flame Rating | 1.5 mm | UL 94 | V-0 | |
Flame Rating | 3.0 mm | UL 94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.