Technical Data Sheet
Electrical | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | IEC 60093 | -- | ohms |
Comparative Tracking Index | | IEC 60112 | -- | V |
Volume Resistivity | | IEC 60093 | 10000000000000 | ohms·cm |
Dielectric Strength | | IEC 60243-1 | 27 | KV/mm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Notched Impact Strength | -30℃ -30°C | ISO 179/1eA | 5 | kJ/m² |
Charpy Notched Impact Strength | 23℃ 23°C | ISO 179/1eA | 5 | kJ/m² |
Charpy Unnotched Impact Strength | -30℃ -30°C | ISO 179/1eU | 35 | kJ/m² |
Charpy Unnotched Impact Strength | 23℃ 23°C | ISO 179/1eU | 45 | kJ/m² |
物理性能 | Test Condition | Test Method | Test Result | Unit |
---|
Density | | ISO 1183 | 1.37 | g/cm³ |
Modeling Shrinkage | TD Across Flow | ISO 294-4 | 0.8 | % |
Modeling Shrinkage | MD Flow | ISO 294-4 | 0.8 | % |
Moisture Absorption | Saturation,23℃ Saturation, 73°F | ISO 62 | 6.5 | % |
Moisture Absorption | Equilibrium,23℃,50% RH Equilibrium, 73°F, 50% RH | ISO 62 | 2 | % |
机械性能 | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO 527-2 | 5800 | Mpa |
Tensile Strain | Break Break | ISO 527-2 | 3 | % |
Ball Indentation Hardness | | ISO 2039-1 | 170 | Mpa |
Tensile Strength | Break Break | ISO 527-2 | 75 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flammability level | 0.8 mm 0.8 mm | IEC 60695-11-10, -20 | HB | |
Thermal | Test Condition | Test Method | Test Result | Unit |
---|
Heat Deflection Temperature | 1.8 MPa,Unannealed 264 psi, Unannealed | ISO 75-2/A | 110 | °C |
Heat Deflection Temperature | 8.0 MPa,Unannealed 1160 psi, Unannealed | ISO 75-2/C | 70 | °C |
Coefficient of Linear Thermal Expansion | MD Flow | ISO 11359-2 | 0.000080 | 1/℃ |
Coefficient of Linear Thermal Expansion | TD Transverse | ISO 11359-2 | 0.000080 | 1/℃ |
Melting Temperature | | ISO 11357-3 | 260 | °C |
Continuous Use Temperature | -- -- 3 3 | ISO 2578 | 100 到 120 | °C |
Continuous Use Temperature | -- -- 4 4 | 内部方法 | 220 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.