Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 2.00 | cm3/10min |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ISO527-2/1A/1 | 4900 | Mpa |
Tensile Stress | Break | ISO527-2/1A/5 | 77.0 | Mpa |
Tensile Strain | Break | ISO527-2/1A/5 | 4.5 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/Bf | 179 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/Af | 101 | °C |
Vicat Softening Temperature | -- | ISO306/A50 | 213 | °C |
Vicat Softening Temperature | -- | ISO306/B50 | 128 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 36 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Ball Indentation Hardness | H358/30 | ISO2039-1 | 97.0 | Mpa |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Burning Rate | | ISO3795 | <100 | mm/min |
Flammability level | 1.5mm | IEC60695-11-10,-20 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.