Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | Across Flow | ISO 294-4 | 0.20 | % |
Modeling Shrinkage | 流量 | ISO 294-4 | 0.70 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Break | ISO 527-2 | 136 | Mpa |
Tensile Strain | Break | ISO 527-2 | 5.0 | % |
Tensile Modulus | | ISO 527-2 | 7400 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45 MPa, Unannealed | ISO 75-2/B | 195 | °C |
Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 185 | °C |
Vicat Softening Temperature | | ISO 306/B50 | 190 | °C |
Melting Temperature | | ISO 11357-3 | 202 | °C |
Melting Temperature | Renewable Carbon Conent | ISO 11357-3 | > 95 | % |
Injection | Test Condition | Test Method | Test Result | Unit |
---|
Processing (Melt) Temp | | | 240 到 290 | °C |
Mold Temperature | | | 60 到 110 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 95 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO 179/1eU | 95 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.