Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	Flow : 24hr	ASTM D955	1.4	%
	Modeling Shrinkage	Across Flow : 24hr	ASTM D955	1.6	%
		Modeling Shrinkage	Across Flow : 24hr	ISO 294-4	1.3	%
		Modeling Shrinkage	Modeling Shrinkage	流量 : 24hr	ISO 294-4	1.5	%
Moisture Absorption	24 hr, 50% RH	ASTM D570	0.16	%
Moisture Absorption	Moisture Absorption	Equilibrium, 23°C, 50% RH	ISO 62	0.29	%

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Tensile Modulus	-- 1	ASTM D638	6130	Mpa
Tensile Modulus	Tensile Modulus	--	ISO 527-2/1	5800	Mpa
Tensile Elongation	Yield	ASTM D638	3.6	%
	Tensile Elongation	Yield	ISO 527-2	2.3	%
		Tensile Elongation	Break	ASTM D638	2.6	%
		Tensile Elongation	Tensile Elongation	Break	ISO 527-2	4.0	%
Flexural Modulus	--	ASTM D790	5300	Mpa
Flexural Modulus	Flexural Modulus	--	ISO 178	6300	Mpa
Flexural Strength		ASTM D790, ISO 178	92.0	Mpa
Tensile Strength	Yield	ASTM D638	56.0	Mpa
	Tensile Strength	Yield	ISO 527-2	49.0	Mpa
		Tensile Strength	Break	ASTM D638	56.0	Mpa
		Tensile Strength	Tensile Strength	Break	ISO 527-2	46.0	Mpa
Coefficient of Friction	Dynamic	ASTM D3702	0.50
Coefficient of Friction	Coefficient of Friction	Static	ASTM D3702	0.43
Specific Wear Rate		ASTM D3702	1.9E+8	10^-8 mm³/N·m

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	161	°C
	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	132	°C
	Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 3	ISO 75-2/Af	147	°C

Injection	Test Result	Unit
Drying Time	4.0	hr
Rear Temperature	175 到 190	°C
Middle Temperature	195 到 205	°C
Front Temperature	210 到 220	°C
Back Pressure	0.200 到 0.300	Mpa
Screw Speed	30 到 60	rpm
Drying Temperature	80	°C
Processing (Melt) Temp	200 到 215	°C
Mold Temperature	80 到 110	°C

Impact Properties	Test Condition	Test Method	Test Result	Unit
Unnotched Izod Impact Strength	23°C	ASTM D4812	210	J/m
Unnotched Izod Impact Strength	Unnotched Izod Impact Strength	23°C 3	ISO 180/1U	17	kJ/m²
Instrumented Dart Impact	23°C, Energy at Peak	ASTM D3763	9.00	J
Instrumented Dart Impact	Instrumented Dart Impact	--	ISO 6603-2	2.00	J

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.