Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 11 | g/10min |
Melt Mass-Flow Rate | 220°C/10.0kg | ISO1133 | 11 | g/10min |
Modeling Shrinkage | MD:3.20mm | ASTMD955 | 0.40to0.48 | % |
Modeling Shrinkage | TD:3.20mm | ASTMD955 | 0.41to0.51 | % |
Modeling Shrinkage | TD:3.20mm | ISO2577 | 0.41to0.51 | % |
Modeling Shrinkage | MD:3.20mm | ISO2577 | 0.40to0.48 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Stress | Yield | ISO527-2/5 | 53.0 | Mpa |
Tensile Modulus | | ASTMD638 | 2200 | Mpa |
Flexural Modulus | | ISO178 | 2350 | Mpa |
Flexural Modulus | | ASTMD790 | 2300 | Mpa |
Tensile Strength | Break | ASTMD638 | 39.0 | Mpa |
Tensile Strength | Yield | ASTMD638 | 51.0 | Mpa |
Tensile Elongation | Break | ASTMD638 | 30 | % |
Flexural Strength | | ASTMD790 | 77.0 | Mpa |
Flexural Stress | | ISO178 | 79.0 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 86.0 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 98.0 | °C |
Vicat Softening Temperature | | ISO306/B50 | 98.0 | °C |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Notched Izod Impact Strength | 23°C | ISO180/1A | 6.0 | kJ/m² |
CharpyNotchedImpactStrength5 | 23°C | ISO179/1eA | 5.8 | kJ/m² |
hardness | Test Condition | Test Method | Test Result | Unit |
---|
Rockwell Hardness | R-Scale | ASTMD785 | 114 | |
Rockwell Hardness | R-Scale | ISO2039-2 | 114 | |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 1.5to3.0mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.