Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Modeling Shrinkage | MD:3.00mm | | 2.1 | % |
Modeling Shrinkage | MD:3.00mm | | 2.0 | % |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.18 | % |
Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 6.0 | g/10min |
Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 7.5 | g/10min |
Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 6.10 | cm3/10min |
Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 4.70 | cm3/10min |
Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.19 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Nominal Tensile Strain at Break | | ISO527-2 | 15 | % |
Nominal Tensile Strain at Break | | ISO527-2 | 18 | % |
Flexural Stress | | ISO178 | 67.0 | Mpa |
Flexural Stress | | ISO178 | 77.0 | Mpa |
Tensile Stress | Yield | ISO527-2 | 44.0 | Mpa |
Tensile Stress | Yield | ISO527-2 | 52.0 | Mpa |
Tensile Strain | Yield | ISO527-2 | 8.0 | % |
Tensile Modulus | | ISO527-2 | 2650 | Mpa |
Tensile Modulus | | ISO527-2 | 2400 | Mpa |
Flexural Modulus | | ISO178 | 2400 | Mpa |
Flexural Modulus | | ISO178 | 2200 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Deflection Temperature Under Load? | 0.45MPa,Unannealed | ISO75-2/B | 151 | °C |
Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 96.0 | °C |
Linear thermal expansion coefficient | MD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
Linear thermal expansion coefficient | TD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
Melting temperature | | ISO11357-3 | 166 | °C |
0.45MPa, Unannealed | | ISO75-2/B | 154 | °C |
1.8MPa, Unannealed | | ISO75-2/A | 97.0 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Comparative Tracking Index | | IEC60112 | 600 | V |
Dielectric Strength | 1.00mm | IEC60243-1 | 25 | KV/mm |
Dielectric Strength | 3.00mm | IEC60243-1 | 16 | KV/mm |
Surface Resistivity | | IEC60093 | 1E+16 | ohms |
Volume Resistivity | | IEC60093 | 1E+14 | ohms·cm |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Charpy Unnotched Impact Strength | 23°C | ISO179 | 60 | kJ/m² |
Charpy Unnotched Impact Strength | 23°C | ISO179 | 50 | kJ/m² |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
UL flame retardant rating | 0.800mm | UL94 | HB | |
UL flame retardant rating | 0.8mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.