Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.16 | % |
Flow:24hr | | ASTMD955 | 0.040到0.10 | % |
Flow:24hr | | ASTMD955 | 0.040到0.10 | % |
Flow:24hr | | ASTMD955 | 0.30到0.40 | % |
Flow:24hr | | ASTMD955 | 0.30到0.40 | % |
Across Flow:24hr | | ISO294-4 | 0.32到0.41 | % |
Across Flow:24hr | | ISO294-4 | 0.32到0.41 | % |
Flow:24hr | | ISO294-4 | 0.040到0.13 | % |
Flow:24hr | | ISO294-4 | 0.040到0.13 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
--1 | | ASTMD638 | 8780 | Mpa |
--1 | | ASTMD638 | 8780 | Mpa |
fracture | | ASTMD638 | 110 | Mpa |
fracture | | ISO527-2 | 109 | Mpa |
fracture | | ASTMD638 | 110 | Mpa |
fracture | | ISO527-2 | 109 | Mpa |
fracture | | ASTMD638 | 2.1 | % |
fracture | | ISO527-2 | 2.0 | % |
fracture | | ASTMD638 | 2.1 | % |
fracture | | ISO527-2 | 2.0 | % |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
1.8MPa, Unannealed,3.20mm | | ASTMD648 | 137 | °C |
Linear thermal expansion coefficient | MD:-40to40°C | ASTME831,ISO11359-2 | 1.8E-05 | cm/cm/°C |
Linear thermal expansion coefficient | TD:-40to40°C | ASTME831,ISO11359-2 | 5E-05 | cm/cm/°C |
0.45MPa, Unannealed,3.20mm | | ASTMD648 | 145 | °C |
1.8MPa, Unannealed,64.0mm Span | | ISO75-2/Af | 146 | °C |
Electrical performance | Test Condition | Test Method | Test Result | Unit |
---|
Surface Resistivity | | ASTMD257 | 10到1.0E+5 | ohms |
Surface Resistivity | | ASTMD257 | 10到1.0E+5 | ohms |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
23°C | | ASTMD256 | 74 | J/m |
23°C | | ASTMD4812 | 490 | J/m |
23°C | | ASTMD256 | 74 | J/m |
23°C | | ASTMD4812 | 490 | J/m |
23°C2 | | ISO180/1A | 6.4 | kJ/m² |
23°C2 | | ISO180/1A | 6.4 | kJ/m² |
23°C3 | | ISO180/1U | 33 | kJ/m² |
23°C3 | | ISO180/1U | 33 | kJ/m² |
23°C,EnergyatPeakLoad | | ASTMD3763 | 15.5 | J |
-- | | ISO6603-2 | 3.36 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.