Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | | | 0.32 | % |
| Moisture Absorption | Equilibrium,23°C,50%RH | ISO62 | 0.73 | % |
| Melt Mass-Flow Rate | 280°C/5.0kg | ISO1133 | 13 | g/10min |
| Melt Volume flow Rate | 280°C/5.0kg | ISO1133 | 8.50 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break | ISO527-2 | 208 | Mpa |
| Tensile Strain | Break | ISO527-2 | 2.0 | % |
| Tensile Modulus | | ISO527-2 | 16000 | Mpa |
| Flexural Modulus | | ISO178 | 14300 | Mpa |
| Flexural Stress | | ISO178 | 349 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,Unannealed | ISO75-2/A | 232 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1.1E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 5.6E-05 | cm/cm/°C |
| Melting temperature | | ISO11357-3 | 257 | °C |
| Glass Transition Temperature | | ISO11357-2 | 87.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Relative Permittivity | 100Hz | IEC60250 | 4.20 | |
| Relative Permittivity | 1MHz | IEC60250 | 4.10 | |
| Dissipation Factor? | 100Hz | IEC60250 | 5.5E-03 | |
| Dissipation Factor? | 1MHz | IEC60250 | 6.7E-03 | |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | 23°C | ISO179 | 90 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 1.6mm | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.