PA66/PTFE Grilon® TSG30-4 LF15 EMS-CHEMIE SWITZERLAND
171
- Unit Price:
- $7193 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 82.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Thermal stability
- Application Areas:Automotive Applications Profile
- Color:--
- Grade:--
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | TD | ISO 294-4 | 干燥｜0.70 | % |
| MD | ISO 294-4 | 干燥｜0.20 | % | |
| Moisture Absorption | Saturation, 23°C | ISO 62 | 干燥｜4.0 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 干燥｜1.5 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Break | ISO 527-2 | 干燥｜150 | Mpa |
| Break | ISO 527-2 | 调节后｜90.0 | Mpa | |
| Tensile Strain | Break | ISO 527-2 | 干燥｜2.5 | % |
| Break | ISO 527-2 | 调节后｜4.5 | % | |
| Tensile Modulus | ISO 527-2 | 干燥｜10500 | Mpa | |
| ISO 527-2 | 调节后｜6500 | Mpa | ||
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 干燥｜9.0 | kJ/m² |
| -30°C | ISO 179/1eA | 调节后｜8.5 | kJ/m² | |
| 23°C | ISO 179/1eA | 干燥｜9.5 | kJ/m² | |
| 23°C | ISO 179/1eA | 调节后｜14 | kJ/m² | |
| Charpy Unnotched Impact Strength | -30°C | ISO 179/1eU | 干燥｜60 | kJ/m² |
| -30°C | ISO 179/1eU | 调节后｜60 | kJ/m² | |
| 23°C | ISO 179/1eU | 干燥｜65 | kJ/m² | |
| 23°C | ISO 179/1eU | 调节后｜70 | kJ/m² | |
| Ball Indentation Hardness | ISO 2039-1 | 干燥｜255 | Mpa | |
| ISO 2039-1 | 调节后｜130 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Continuous Use Temperature | --3 | ISO 2578 | 干燥｜100 到120 | °C |
| --4 | 内部方法 | 干燥｜220 | °C | |
| Melting Temperature | ISO 11357-3 | 干燥｜260 | °C | |
| Deflection Temperature Under Load? | 1.8 MPa, Unannealed | ISO 75-2/A | 干燥｜235 | °C |
| 8.0 MPa, Unannealed | ISO 75-2/C | 干燥｜165 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface Resistivity | IEC 60093 | 调节后｜1.0E+10 | ohms | |
| Volume Resistivity | IEC 60093 | 干燥｜1.0E+12 | ohms·cm | |
| IEC 60093 | 调节后｜1.0E+12 | ohms·cm | ||
| Dielectric Strength | IEC 60243-1 | 干燥｜28 | KV/mm | |
| IEC 60243-1 | 调节后｜26 | KV/mm | ||
| Comparative Tracking Index | IEC 60112 | 调节后｜600 | V |
| Other | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flammability level | 0.8 mm | IEC 60695-11-10, -20 | 干燥｜V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.