Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD | 内部方法 | 1.3 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Stress | Break | ISO527-2/5 | 51.0 | Mpa |
| Tensile Strain | Break | ISO527-2/5 | 2.7 | % |
| Flexural Modulus | | ISO178 | 2700 | Mpa |
| Flexural Stress | --3 | ISO178 | 82.0 | Mpa |
| Flexural Stress | --4 | ISO178 | 83.0 | Mpa |
| Tensile Modulus | | ISO527-2/1 | 3100 | Mpa |
| Flexural Strain (Break) | | ISO178 | 4.5 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 149 | °C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 89.0 | °C |
| Linear thermal expansion coefficient | MD：23to60°C | ISO11359-2 | 7.3E-05 | cm/cm/°C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 3.0 | kJ/m² |
| Unnotched Izod Impact Strength | 23°C | ISO180/1U | 15 | kJ/m² |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 3.0mm,TestingbySABIC | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.