PA66/PTFE LNP™ LUBRICOMP™ RFL-4033 SABIC INNOVATIVE US
146
- Unit Price:
- $4854 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 42MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515
serv********
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:wear resistant enhance
- Application Areas:Electrical appliances Electronic and Electrical
- Color:--
- Grade:Injection grade
Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | MD：24hr | ASTMD955 | 0.50to0.70 | % |
| TD：24hr | ASTMD955 | 1.6to1.8 | % | |
| TD:24hr | ISO294-4 | 1.7 | % | |
| MD:24hr | ISO294-4 | 0.64 | % | |
| Moisture Absorption | 24hr,50%RH | ASTMD570 | 0.60 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Stress | Break | ISO527-2 | 118 | Mpa |
| Yield | ISO527-2 | 118 | Mpa | |
| Tensile Strain | Break | ISO527-2 | 3.1 | % |
| Yield | ISO527-2 | 3.1 | % | |
| Tensile Modulus | ISO527-2/1 | 6440 | Mpa | |
| Tensile Elongation | Yield | ASTMD638 | 3.1 | % |
| Break | ASTMD638 | 3.1 | % | |
| Flexural Modulus | ASTMD790 | 5520 | Mpa | |
| ISO178 | 5800 | Mpa | ||
| Flexural Strength | ASTMD790 | 179 | Mpa | |
| Flexural Stress | ISO178 | 183 | Mpa | |
| Coefficient of Friction | Dynamic | ASTMD3702Modified | 0.40 | |
| Static | ASTMD3702Modified | 0.45 | ||
| Tensile Modulus | ASTMD638 | 6890 | Mpa | |
| Tensile Strength | Yield | ASTMD638 | 120 | Mpa |
| Break | ASTMD638 | 120 | Mpa | |
| Specific Wear Rate | ASTMD3702Modified | 19.5 | 10^-10in^5-min/ft-lb-hr |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 243 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 260 | °C | |
| Deflection Temperature Under Load? | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 261 | °C |
| 1.8MPa,Unannealed,3.20mm | ASTMD648 | 247 | °C | |
| Linear thermal expansion coefficient | MD：-40to40°C | ASTME831 | 8.3E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 8.3E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 4E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 3.9E-05 | cm/cm/°C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Notched Izod Impact Strength | 23°C | ISO180/1A | 6.7 | kJ/m² |
| UnnotchedIzodImpactStrength3 | 23°C | ISO180/1U | 35 | kJ/m² |
| Instrumented Dart Impact | 23°C,EnergyatPeakLoad | ASTMD3763 | 7.60 | J |
| Multi-Axial Instrumented Impact Energy | ISO6603-2 | 2.10 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.