Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Apparent Density | | ISO 60 | 0.50 | g/cm³ |
| Melt Mass-Flow Rate | 190°C/21.6 kg | ISO 1133 | < 0.10 | g/10 min |
| Viscosity Number (Reduced Viscosity) | -- | ISO 1628 | 1700.0 | ml/g |
| Viscosity Number (Reduced Viscosity) | -- 3 | ISO 1628 | 1900.0 | ml/g |
| Viscosity Number (Reduced Viscosity) | Elongational Stress F - 150/10 | ISO 11542-2 | 0.120 | Mpa |
| Molecular Weight Distribution | | | 3700000 | g/mol |
| Particle Size Distribution | | | Pellet | |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Wear by Sandslurry Method 6 | | 内部方法 | 130 | |
| Tensile Modulus | | ISO 527-2/1B | 800 | Mpa |
| Tensile Stress | Yield | ISO 527-2/1B | 22.0 | Mpa |
| Tensile Stress | Break | ISO 527-2/1B | 37.0 | Mpa |
| Tensile Stress | 50% Strain | ISO 527-2/1B | 19.0 | Mpa |
| Tensile Strain | Yield | ISO 527-2/1B | 12 | % |
| Nominal Tensile Strain at Break | | ISO 527-2/1B | 430 | % |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ISO 306/B50 | 80.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC 60093 | > 1.0E+12 | ohms |
| Volume Resistivity | | IEC 60093 | > 1.0E+14 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Double 14°V-Notch Strength | 23°C | ISO 11542-2 | 190 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore Hardness | Shore D, 15 sec | ISO 868 | 62 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.