Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD:2.00mm | 内部方法 | 1.5 | % |
| Modeling Shrinkage | TD:2.00mm | 内部方法 | 1.3 | % |
| Moisture Absorption | 24hr | ASTMD570 | <0.010 | % |
| Spiral Flow | | 内部方法 | 33.0 | CM |
| PVLimit3 | | 内部方法 | >0.50 | MPa·m/s |
| Melt Mass-Flow Rate | 190°C/10.0kg | JISK7210 | 7.0 | g/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Coefficient of Friction | Dynamic | 内部方法 | 0.17 | |
| Abrasion Loss | | 内部方法 | 220 | 10^-8mm³/N·m |
| Tensile Elongation | Break,23°C | ASTMD638 | 9.0 | % |
| Flexural Modulus | 23°C,3.00mm,48.0mmSpan | ASTMD790 | 2300 | Mpa |
| Tensile Strength | Break,23°C | ASTMD638 | 47.0 | Mpa |
| Flexural Strength | 23°C,3.00mm,48.0mmSpan | ASTMD790 | 45.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,Unannealed | ASTMD648 | 91.0 | °C |
| Linear thermal expansion coefficient | MD | ASTMD696 | 1.2E-04 | cm/cm/°C |
| Vicat Softening Temperature | | ASTMD15256 | 130 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric Strength | | ASTMD149 | 60 | KV/mm |
| Dielectric Constant | 23°C | ASTMD150 | 2.50 | |
| Volume Resistivity | | ASTMD257 | 1.0E+17到1.0E+18 | ohms·cm |
| Dissipation Factor? | 1MHz | ASTMD150 | 1.0E-4到2.0E-4 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R-Scale | ASTMD785 | 63 | |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| HeatGenerationTemperature3 | | 内部方法 | 75 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.