Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | Flow | ISO 294 | 0.3 | % |
| Modeling Shrinkage | 垂直 | ISO 294 | 0.7 | % |
| Moisture Absorption | 23℃ 24hr | ISO 62 | 4.8 | % |
| Moisture Absorption | 23°C50RH | ISO 62 | 1.6 | % |
| proportion | | ISO 1183 | 1.46 | g/cm³ |
| Melt Mass-Flow Rate | 5kg | ISO 1133 | 45 | cm3/10mir |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | | ISO 179 | 8 | kJ/m² |
| Tensile Modulus | 23℃ | ISO 527 | 1100 | Mpa |
| Tensile Strength | 23℃ | ISO 527 | 150 | Mpa |
| Tensile Elongation | 23℃ | ISO 527 | 2.5 | % |
| Flexural Strength | 23℃ | ISO 178 | 240 | Mpa |
| Charpy Unnotched Impact Strength | 23℃ | ISO 179 | 65 | kJ/m² |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Thermal Conductivity | | DIN 52612 | 0.37 | W/(m.K) |
| Deflection Temperature Under Load? | Unannealed1.8MPa | ISO 75 | 220 | °C |
| Melting temperature | | ISO 11357 | 290 | °C |
| Coefficient of Linear Thermal Expansion | Flow | ISO 11359 | 2.3E-5 | cm/cm/℃ |
| Coefficient of Linear Thermal Expansion | 垂直 | ISO 11359 | 7E-5 | cm/cm/℃ |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | IEC 60093 | 1E17 | Ω.cm |
| Dielectric Constant | 1MHz | IEC 60250 | 0.015 | |
| Flame Rating | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating (1.60 mm) | | UL94 | V-0 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.