PBT/PET Pocan® ECOT3230 LANXESS GERMANY
185
- Unit Price:
- $2149 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 23MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 260℃，5 kg 260℃/5.0 kg | ISO 1133 | 30 | cm3/10min |
| Density (73 ° F) | ISO 1183 | 1.55 | g/cm³ | |
| Apparent density | ISO 60 | 0.8 | g/cm³ | |
| Water absorption rate | Saturation，23℃ Saturation，23℃ | ISO 62 | 0.3 | % |
| Equilibrium，23℃，50% RH Equilibrium，23℃，50% RH | ISO 62 | 0.1 | % | |
| Shrinkage rate | TD：270℃，2.0 mm Across Flow : 518°F, 0.0787 in 2 2 | ISO 294-4 | 0.9 | % |
| TD：120℃，2.0 mm，2 hrs Across Flow : 120°C, 2 hr, 2.00 mm 3 3 | ISO 294-4 | 0.2 | % | |
| MD：270℃，2.0 mm Flow : 518°F, 0.0787 in 2 2 | ISO 294-4 | 0.3 | % | |
| MD：120℃，2.0 mm，2 hrs Flow : 120°C, 2 hr, 2.00 mm 3 3 | ISO 294-4 | 0.1 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending strength | 23℃ 23℃ 4 | ISO 178 | 230 | Mpa |
| Tensile strength | Break，23℃ Break，23℃ | ISO 527-2/5 | 145 | Mpa |
| Tensile modulus | 23℃ 23℃ | ISO 527-1-2 | 10400 | Mpa |
| Bending modulus 4 | 23℃ 23℃ 4 | ISO 178-A | 10300 | Mpa |
| Bending strain | 3 | % | ||
| Tensile strain | Break，23℃ Break，23℃ | ISO 527-2/5 | 2.8 | % |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the leakage trace index | Solution A Solution A | IEC 60112 | 250 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap | -30℃ -30°C | ISO 179/1eA | < 10 | kJ/m² |
| 23℃ 23°C | ISO 179/1eA | < 10 | kJ/m² | |
| Impact strength of cantilever beam gap | -30℃ -30°C | ISO 180-1A | < 10 | kJ/m² |
| 23℃ 23°C | ISO 180-1A | < 10 | kJ/m² | |
| Cantilever beam without notch impact strength | -30℃ -30°C | ISO 180/1U | 55 | kJ/m² |
| 23℃ 23°C | ISO 180/1U | 55 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30℃ -30°C | ISO 179/1eU | 55 | kJ/m² |
| 23℃ 23°C | ISO 179/1eU | 65 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | B120 B120 | ISO 306/B120 | 205 | °C |
| Melting temperature | ISO 11357-3 | 225 to 250 | °C | |
| Linear coefficient of thermal expansion | TD：23~55℃ TD：23 to 55℃ | ISO 11359-2 | 0.000090 | 1/℃ |
| MD：23~55℃ MD：23 to 55℃ | ISO 11359-2 | 0.000030 | 1/℃ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.